Corrosion behaviour of direct current and active screen plasma carburised AISI 316 stainless steel in boiling sulphuric acid solutions

Abstract

Active screen plasma is a recently developed plasma surface alloying technique, which has shown potential for addressing some drawbacks associated with conventional direct current plasma processes. In this study, the corrosion performance of untreated, direct current and active screen plasma carburised AISI 316 was investigated by immersion in a boiling solution of sulphuric acid. The experimental results show that the corrosion behaviour of expanded austenite produced by low temperature plasma carburising is controlled by the type and density of surface defects; the corrosion properties of the active screen plasma carburised material are superior to that produced by direct current plasma because of the significantly reduced edge effect and surface defects; and the bias level used in the active screen carburising treatment has a profound effect on the corrosion performance of the material. Based on the experimental results, the corrosion mechanisms involved are discussed.

Keywords:

• Active screen
• Plasma carburising
• Austenitic stainless steel
• Corrosion
• Sulphuric acid

Mr Corujeira Gallo would like to thank Roberto Rocca Education Programme, The University of Birmingham and EU AlBan Programme (scholarship E05M060379AR) for their financial support.