Microstructure and martensitic transformation and mechanical properties of cast Ni rich NiTiCo shape memory alloys

Abstract

The influence of Co additions on the microstructure, second phase precipitates, phase transformation and mechanical properties of cast Ni_51−xTi₄₉Co_x (x = 0, 0·5, 1·5 and 4 at-%) shape memory alloys was investigated. At the expense of Ni, Co added to NiTi alloy significantly increases the martensitic transformation temperature. The matrix phase in the microstructure of Ni₅₁Ti₄₉Co₀ alloy is the austenite phase (B2) in addition to martensite phase (B19′) and precipitates of NiTi intermetallic compounds. However, the parent phase in the other three alloys, Ni_50·5Ti₄₉Co_0·5, Ni_49·5Ti₄₉Co_1·5 and Ni₄₇Ti₄₉Co₄, is martensite. Ti₂Ni phase was found in the microstructures of the all investigated alloys; however, Ni₃Ti₂ phase precipitated only in the NiTi alloy with 0 at-%Co. The volume fraction of Ti₂Ni phase decreased by the additions of 0·5 and 1·5 at-%Co, while it is slightly increased with 4 at-%Co. The hardness value of NiTi alloy is affected by Co additions.

Keywords:

• Ni rich NiTiCo shape memory alloys
• Microstructure
• Martensitic transformation
• X-ray diffraction
• Hardness