Fabrication of in situ TiB₂–TiC reinforced steel matrix composites by spark plasma sintering

Abstract

In situ TiB₂ and TiC particulates reinforced steel matrix composites have been fabricated using cheap ferrotitanium and boron carbide powders by spark plasma sintering (SPS) technique. The sintering behaviour and the formation mechanism of the composite were studied. The results show that when the composite was sintered at 1050°C for 5 min, the maximum relative density and hardness of the composite are 99·2% and 83·8 HRA respectively. The phase evolution of the composite during sintering indicates that the TiB₂ and TiC reinforcements were formed in situ as follows: first, the solid/solid interface reaction between Fe₂Ti and B₄C, resulting in the formation of a small amount of TiB₂ and TiC below 950°C; second, the solid–liquid solution precipitation reaction in the Fe–Ti–B–C system, resulting in the formation of the main TiB₂ and TiC reinforcements at ∼1000°C.

Keywords:

• Composite materials
• TiB₂–TiC
• Spark plasma sintering
• Microstructure