Abstract
Influence of the concentration (0–1×10−3M) of Mo(IV) compounds on the electroless deposition of Co–Mo–P alloy from alkaline citrate bath was investigated. The changes of the plating potential, mass of the deposits and hydrogen evolution as well as composition and morphology of the deposits with the concentration of additives were determined. Similar behaviour was observed for all compounds. Increase in the concentration in the bath was accompanied by inhibition of Co–Mo–P deposition and only traces of deposits were obtained at 1×10−3M Mo(VI). Molybdenum content in the deposits was low and oxygen was detected in the layers produced at 5×10−4 and 1×10−3M Mo(VI). Such changes corresponded to a gradual evolution of the morphology of the deposits from needle to fine grained structure, but Na2MoO4 produced deposits of the best quality. Adsorption of
ions at the metal/electrolyte interface was proposed as responsible for phenomena observed in the Co–Mo–P system.
Keywords:
This research work has been supported by the Polish Ministry of Science and Higher Education under project no. 11·11·180·374.