Impact of ribbon width on magnetoimpedance and permeability of Fe69.2Co7.7Cu0.6Nb2.5Si11B9 soft magnetic alloy

Y. DingSchool of Electronics Information Engineering, Tianjin Key Laboratory of Film Electronic and Communication Devices, Tianjin University of Technology, Tianjin, China
,
R. TianSchool of Electronics Information Engineering, Tianjin Key Laboratory of Film Electronic and Communication Devices, Tianjin University of Technology, Tianjin, China
,
K. XueSchool of Electronics Information Engineering, Tianjin Key Laboratory of Film Electronic and Communication Devices, Tianjin University of Technology, Tianjin, China
,
X. WangSchool of Electronics Information Engineering, Tianjin Key Laboratory of Film Electronic and Communication Devices, Tianjin University of Technology, Tianjin, China
,
Y. ShiSchool of Electronics Information Engineering, Tianjin Key Laboratory of Film Electronic and Communication Devices, Tianjin University of Technology, Tianjin, China
&
X. MaSchool of Material Science and Engineering, Tianjin University of Technology, Tianjin, ChinaCorrespondence[email protected]
Pages 337-341 | Received 27 Mar 2015, Accepted 02 Jul 2015, Published online: 02 Feb 2016
 
Sample our Physical Sciences journals, sign in here to start your FREE access for 14 days

Abstract

Fe69.2Co7.7Cu0.6Nb2.5Si11B9 soft magnetic alloy ribbons of different widths, 4.4 and 8.0 mm respectively, were used for the research work. The influences of structural modifications induced by heat treatment on magnetoimpedance effect and permeability have been studied. In as quenched state and annealed at temperatures < 773 K, 4.4 mm wide ribbons showed larger MI values than the 8.0 mm wide ribbons. After being annealed at temperatures >823 K, the MI values of the 8.0 mm wide ribbons were slightly higher than those of 4.4 mm wide ribbons due to the improved soft magnetic properties. With controlled heat treatment at 853 K, a maximum MI ratio of 82% was detected for the 8.0 mm wide ribbon.

Log in via your institution

Access through your institution

Log in to Taylor & Francis Online

Restore content access

Restore content access for purchases made as guest
Purchase options * Save for later
PDF download + Online access
  • 48 hours access to article PDF & online version
  • Article PDF can be downloaded
  • Article PDF can be printed
USD 61.00 Add to cart
* Local tax will be added as applicable

Related Research

People also read lists articles that other readers of this article have read.

Recommended articles lists articles that we recommend and is powered by our AI driven recommendation engine.

Cited by lists all citing articles based on Crossref citations.
Articles with the Crossref icon will open in a new tab.