La Physiochimie Du Ferromanganese Carbure

Abstract

Data from the literature were used to construct activity diagrams for the systems Mn–Fe–C, MnO–CaO–SiO₂ and CaO–Al₂O₃–SiO₂ with 10% MnO. Assuming that the reduction temperature is close to slag melting point, the MnO content required to obtain a 75% Mn alloy can be found. One can also calculate the Si content corresponding to the slag composition. Fixing the allowable %Si it is found that the slag will contain more than 25% MnO in the MnO–CaO–SiO₂ system. The effect of CO pressure is minor. If it is practical to add Al₂O₃ to the slag, its melting point can be lowered sufficiently to obtain slags with 10% MnO in the CaO–Al₂O₃–SiO₂ system while keeping Si in the metal low.

Résumé

Des données de la littérature ont été employées pour construire les diagrammes d'activité des systèmes Mn–Fe–C, MnO–CaO–SiO₂, et CaO–Al₂O₃–SiO₂ it 10% de MnO. En admettant que la température de la zone de réduction est proche de celle de fusion du laitier, on trouve la teneur en MnO nécessaire pour obtenir l'alliage à 75% de Mn. La quantité de Si réduit a également été déterminée. Le calcul montre qu'en fixant la teneur finale silicium à moins de 0.5% la teneur en MnO doit être supérieure à 25% . dans les laitiers MnO–CaO–SiO₂. La pression de CO n'a guere d'effet. S'il est pratique d'ajouter du Al₂O₃ au laitier pour en abaisser le point de fusion on peut obtenir avec un laiter it 10 % de MnO un alliage pour lequelle Si ne dépasse pas les bornes permises.