Effect of surface organic coatings of cellulose nanocrystals on the viability of mammalian cell lines

, , , , &
Pages 123-136 | Published online: 28 Sep 2017

Abstract

Cellulose nanocrystals (CNCs) have emerged as promising candidates for a number of bio-applications. Surface modification of CNCs continues to gain significant research interest as it imparts new properties to the surface of the nanocrystals for the design of multifunctional CNCs-based materials. A small chemical surface modification can potentially lead to drastic behavioral changes of cell-material interactions thereby affecting the intended bio-application. In this work, unmodified CNCs were covalently decorated with four different organic moieties such as a diaminobutane fragment, a cyclic oligosaccharide (β-cyclodextrin), a thermoresponsive polymer (poly[N-isopropylacrylamide]), and a cationic aminomethacrylamide-based polymer using different synthetic covalent methods. The effect of surface coatings of CNCs and the respective dose-response of the above organic moieties on the cell viability were evaluated on mammalian cell cultures (J774A.1 and MFC-7), using 3-(4,5-dimethylthiazol-2-yl)-2,5-diphe-nyltetrazolium bromide and lactate dehydrogenase assays. Overall, the results indicated that cells exposed to surface-coated CNCs for 24 h did not display major changes in cell viability, membrane permeability as well as cell morphology. However, with longer exposure, all these parameters were somewhat affected, which appears not to be correlated with either anionic or cationic surface coatings of CNCs used in this study.

Introduction

With the rapid development of nanoscience and nanotechnology, cellulose has revived in the form of nanocelluloses with a pressing demand for their large-scale production for various potential high-end sustainable applications in diverse fields such as materials science, biomedicine, electronics, catalysis etc.Citation1,Citation2 Among the family of the nanocelluloses are cellulose nanocrystals (CNCs), which have recently gained significant interest in both academic and industrial research. CNCs are nanoscale-sized, needle- or rod-like particles typically derived from the acid hydrolysis of native cellulose under controlled conditions. Their high mechanical strength and unique physicochemical properties made them attractive building blocks for the development of new functional cellulose-based nanomaterials.Citation3Citation5 Other than their perceived use in high-performance nanocomposites, CNCs have turned into promising materials for biomedical applications due to their special surface chemistry, environmental biodegradability, biocompatibility and low toxicity.Citation6,Citation7 The exposure to CNCs via occupational, environmental, consumer and biomedical arenas is expected to increase rapidly given the high interest in the large-scale production of CNCs (particularly wood-based CNCs) in order to meet both academic and industrial research demands. CNCs possess high aspect ratio and stiffness similar to asbestos and carbonaceous fibers that have been linked with high toxicity.Citation8 As such, recent efforts have focused on evaluating the health effects associated with CNCs exposures given the wide potential applications of CNCs in the biomedical fields such as drug and gene delivery, bioimaging, biosensing, tissue engineering and enzyme/protein immobilization scaffolds.Citation9 A recent review by Roman provides a detailed account on current literature on the pulmonary, oral, dermal and cytotoxicity of CNCs, which highlighted the importance of careful sample characterization and the exclusion of the interfering effects of endotoxins and cytotoxic contaminants during the assessment of the potential adverse health effects of CNCs.Citation10 Shatkin and Kim proposed a life cycle risk assessment (LCRA) framework called NANO LCRA that was employed for pre-commercial screening of selected applications of nanocelluloses (CNCs and cellulose nanofibrils). This systematic method identified and assessed the potential risks of nanocelluloses from occupational, consumer and environmental exposures throughout the product life cycle.Citation11 Camarero-Espinosa et al discussed the importance of how knowledge gained from studying the biological impact of other nanomaterials could provide a basis for future research strategies to assess the human health risks that could arise from the use of CNCs.Citation12 With regard to the evaluation of the cytotoxicity effects of CNCs, several studies have been carried out using CNCs obtained from different cellulosic sources, preparation procedures as well as with a variety of cell lines.Citation13Citation25 Most of these studies indicated CNCs to be non-toxic at low concentrations, while a few studies showed a dose-dependency of CNCs cytotoxicity.Citation14,Citation18,Citation20,Citation24,Citation25 Discor dant results of CNCs cytotoxicity have also been reported, which could likely be caused by variations in experimental procedures, composition and size of nanoparticles employed, use of varying cellulosic sources and cell types.Citation14,Citation24 While a number of studies have focused mainly on the cytotoxicity of unmodified CNCs and/or fluorescently-labeled CNCs, there are still very limited data regarding the cytotoxicity assessment of surface-modified CNCs, in particular, CNCs coated with structurally functional organic materials for diverse bio-applications.Citation15,Citation22,Citation26 Surface modification of CNCs is crucial for the synthesis of advanced and multifunctional CNCs-based materials and as such, it has been a subject of intense research in the past few years.Citation27Citation29 However, a small chemical modification can potentially lead to drastic behavioral changes of cell-material interactions. It is therefore crucial to evaluate the risks associated with surface-modified CNCs before the latter can be fully exploited for the intended bio-application. Herein, the objective of this study is to synthesize and assess the cytotoxicity of 4 modified CNCs having different surface molecular architectures (ranging from a simple organic moiety to complex polymeric structures) and surface charges (anionic and cationic). In this work, the surface of CNCs was covalently decorated with different functional moieties such as a diaminobutane fragment, a cyclic oligosaccharide (β-cyclodextrin [β-CD]), a thermoresponsive polymer (poly(N-isopropylacrylamide)(poly[NIPAAm])), and a cationic aminomethacrylamide-based polymer to generate CNCs with 4 distinct modified surfaces, termed as CNCs-AMINE, CNCs-β-CD, CNCs-poly(NIPAAm), and CNCs-poly(N-[3-aminopropyl]methacrylamide [APMA]) (). The choice of the above grafted materials is based on their potential use in the biomedical field and to the best of our knowledge, this is the first report of their detailed toxic effects in mammalian cell lines such as J774A.1 (mouse monocyte cells) and MCF-7 (human breast adenocarcinoma cells). In-vitro studies are rapid and cost-effective means to assess cytotoxicity of materials and select the most effective ones for further studies in vivo.

Scheme 1 Synthesis of surface-modified CNCs (A) anionic CNCs-AMINE, (B) anionic CNCs-β-CD, (C) anionic CNCs-poly(NIPAAm) and cationic CNCs-poly(APMA).

Abbreviations: AMINE, amino-functionalized; CNCs, cellulose nanocrystals; CNCs-β-CD, CNCs grafted with β-cyclodextrin; poly-(APMA), poly-(N-3-aminopropyl) methacrylamide; poly-(NIPAAm), poly(N-isopropylacrylamide); rt, room temperature; EDC, N-Ethyl-N′-(3-dimethylaminopropyl)carbodiimide; NHS, N-hydroxysuccinimide; MES, 2-(N-Morpholino)ethanesulfonic acid; THF, tetrahydrofuran; DMAP, 4-(Dimethyamino)pyridine; PMDETA, N,N,N′,N″,N″-pentamethyldiethylenetriamine.
Scheme 1 Synthesis of surface-modified CNCs (A) anionic CNCs-AMINE, (B) anionic CNCs-β-CD, (C) anionic CNCs-poly(NIPAAm) and cationic CNCs-poly(APMA).

Experimental materials

For the purpose of this work, CNCs was obtained from Innotech Alberta (previously Alberta Innovates Technology Futures), a research institute based in AB, Canada. The fibers were prepared by subjecting Whatman™ cotton filter paper to acid hydrolysis using concentrated sulfuric acid. A detailed preparation method is described elsewhere.Citation30 Acetone, copper (I) bromide, β-cyclodextrin, deuterium oxide, 1,3-diaminopropane, epichlorohydrin (99%), ethanol, hydrochloric acid, hydroquinone, methacrylic anhydride, methanol, N,N,N′,N″,N″-pentamethyldiethylenetriamine (PMDETA), 2-propanol and tetrahydrofuran (99%) were obtained from Sigma-Aldrich (St. Louis, MO, USA). Uranyl acetate (dihydrate, 99.6%) and transmission electron microscopy (TEM) grids (400 mesh) were purchased from Electron Microscopy Sciences (Hatfield, PA, USA). Cell lines (mouse monocyte [macrophage] cells [J774A.1] and human breast adenocarcinoma cells [MCF-7]) were obtained from American Type Culture Collection (ATCC, Manassas, VA, USA).

Synthesis of anionic-modified CNCs (CNCs-AMINE, CNCs-poly(NIPAAm), CNCs-β-CD)

Both CNCs-AMINE and CNCs-poly(NIPAAm) were prepared previously in our laboratory and their syntheses and characterization were fully described elsewhere.Citation31,Citation32 CNCs grafted with β-cyclodextrin (CNCs-β-CD) was synthesized according to a previously reported one-step procedure using epichlorohydrin as a coupling reagent under alkaline conditions with slight modifications (Lin and Dufresne 2013).Citation33 β-CD (10.35 g, 9.12 mmol) was added to an aqueous NaOH solution (4 g NaOH in 20 mL of distilled water). A homogeneous suspension of CNCs (1 g in 20 mL of distilled water) was then added in the β-CD alkaline solution, and the mixture was stirred for 30 min. The desired amount of epi-chlorohydrin (5.96 mL, 76 mmol) was added into the reaction mixture, and the reaction was heated at 40°C for 6 h. The epichlorohydrin/cyclodextrin molar ratio was controlled at about 9 to avoid self-cross-linking of β-CD as suggested by Zhao et alCitation34 and Lin and DufresneCitation33 The mixture was centrifuged at 12,000 rpm for 20 min and washed repeatedly with distilled water to ensure removal of both ungrafted β-CD and residual NaOH. For high purity sample, the product was resuspended in water and dialyzed against deionized water for 1 week. The suspension was subsequently freeze-dried to afford a white powder (1.152 g). The grafting efficiency of β-CD on CNCs was evaluated using the method of weight measurement. Three grafting experiments were repeated for an average grafting efficiency of 15.1 wt %, which was in close agreement with previously reported values.Citation33

Synthesis of cationic-modified CNCs

Preparation of the cationic monomer, APMA hydrochloride

APMA hydrochloride was synthesized using a mild and protecting group-free modified version of a previously reported procedure.Citation35 1,3-diaminopropane (8 mL, 96 mmol) in MeOH (50 mL) was added to a stirred solution of 1,3-diaminopro-pane dihydrochloride (13.3 g, 90 mmol) in distilled water (75 mL) at 0°C. After stirring the reaction mixture for 1 h, methacrylic anhydride (28 mL, 184 mmol) and a few crystals of hydroquinone in MeOH (50 mL) were subsequently added dropwise. The reaction mixture was allowed to warm to room temperature and was stirred for 24 h in the dark, after which concentrated hydrochloric acid (25 mL) was added dropwise and stirring was maintained for another 2 h. Removal of solvent under vacuum, followed by washing with acetone produced the crude off-white residue, which upon recrystallization using hot 2-propanol gave rise to the desired APMA hydrochloride as a white solid in 52% yield:Citation1 H NMR (D2O, 400 MHz) δ 1.78 (s, 3H), 1.78–1.75 (m, 2H), 2.88 (t, J=7.5 Hz, 2H), 3.22 (t, J=6.8 Hz, 2H), 5.32 (s, 1H), 5.56 (s, 1H) (Figure S1);Citation13 C NMR (D2O, 100 MHz) δ 17.5, 26.6, 36.1, 36.9, 121.2, 138.8, 172.2 ppm (Figure S2).

Preparation of cationic CNCs-poly(APMA)

The initiator modified-CNCs (CNCs-BriB) was prepared according to our previously reported procedure using a 5:3 ratio of 2-bromoisobutyryl bromide to anhydroglucose units (AGU) in CNCs.Citation36 CNCs-BriB was then grafted with the cationic monomer poly(APMA) via surface-initiated single-electron transfer living radical polymerization (SI-SET-LRP) technique at a ratio of monomer to AGU:(APMA/AGU)=50:3. The preparation of CNCs-poly(APMA) is as follows: CNCs-BriB (350 mg) was dispersed in a H2O:MeOH solvent mixture (100 mL, 1:1) in a 250 mL Schlenk flask. After degassing the reaction mixture under N2 gas, APMA hydrochloride (8.94 g, 50 mmol) and copper (I) bromide (0.143 g, 1 mmol) were added. The suspension was degassed again before addition of PMDETA (0.209 mL, 1 mmol) and reaction mixture was stirred for 24 h at room temperature. The resulting poly(APMA)-grafted CNCs was then centrifuged (3×12,000 rpm at 10°C for 20 min) with 1:3 H2O:MeOH. The residual solid was resuspended in water and dialyzed against deionized water for 1 week with daily changes of deionized water. The suspension was then freeze-dried to afford a white flaky solid.

Instrumentations

Fourier transform infrared spectroscopy (FT-IR)

FT-IR spectra were acquired on a Varian FT-IR spectrophotometer (FTS-7000; Agilent Technologies, Santa Clara, CA, USA) using freeze-dried samples at room temperature under continuous nitrogen purging. Potassium bromide (previously dried in an oven at 150°C) pellets were prepared by grinding and compressing about 2% of the CNCs samples in potassium bromide. Spectra in the range of 4000–400 cm−1 were obtained with a resolution of 4 cm−1 by cumulating 32 scans.

Dynamic light scattering (DLS) and zeta potential measurements

DLS and zeta potential measurements were carried out using a Malvern Zetasizer Nano-S instrument (Malvern Instruments Inc., Westborough, MA, USA). This instrument is equipped with a 4.0 mW He-Ne laser (λ=633 nm) and an avalanche photodiode detector and works at a 173° scattering angle. Prior to the measurements, the CNCs suspensions (0.1 wt %) were equilibrated at room temperature for 10 min in a temperature-regulated cell at 25.0±0.1°C. Comparative effective hydrodynamic diameters and size distributions were obtained using DLS. The reported dhyd (hydrodynamic size) is effective diameter based upon the intensity of scattered light. Both DLS and zeta (ζ) potential measurements were performed at neutral pH. Triplicates were measured for each sample, and averages are reported.

Scanning transmission electron microscopy (STEM)

High resolution scanning electron microscopy (SEM) with a Hitachi model S-4800 or S-5500 apparatus equipped with a field emission source and operating at an accelerating voltage of 30 kV in the transmission mode SEM was used to investigate the morphologies of the samples. The latter were prepared by depositing a drop of the filtered colloidal suspension on a TEM grid for 3 min and the excess liquid was wicked off using filter paper. After drying the TEM grid at room temperature for 3 min, a drop of uranyl acetate solution (2 wt % in water) was deposited on the grid for 5 min for staining and the excess solution was removed using filter paper. Imaging was carried out on samples previously dried for at least 24 h at room temperature.

Cell culture and cytotoxicity assays

Cell culture

The culture of mouse monocyte (macrophage) cells (J774A.1; ATCC) was carried out in Roswell Park Memorial Institute 1640 medium supplemented with 10% fetal bovine serum (FBS), penicillin, streptomycin and L-glutamine. Human breast adenocarcinoma cells (MCF-7; ATCC) were cultured in DMEM medium, supplemented with 10% FBS, essential amino acids (0.1 mM), insulin (10 ug/mL), sodium pyruvate (1 mM), penicillin, streptomycin and L-glutamine. Both cell lines were incubated at 37°C in a 5% CO2-supplemented atmosphere for at least 24 h before the appropriate treatments.

3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay

The cytotoxicity of the unmodified CNCs and its derivatives was assessed by a MTT assay. J774A.1 and MCF-7 cells were seeded in 96-well plates at a density of 5×105 cells/mL. After 24 h, they were treated with unmodified CNCs and its derivatives at 10, 25, 50 and 100 µg/mL, for 24 h or 48 h. After suspending all the compounds in sterile PBS, the medium was removed and the wells were filled with fresh culture medium with 0.5 mg/mL MTT. After 30 min for J774A.1 and 45 min for MCF-7, the medium was removed and the insoluble crystals were solubilized with 200 µL/well of dimethyl sulfoxide. The absorbance was measured at 570 nm using a Synergy H1 Hybrid Multi-Mode Microplate Reader (BioTek, Winoski, VT, USA).

Lactate dehydrogenase (LDH) assay

Unmodified and modified CNCs were suspended as described in MTT assay, and J774A.1 and MCF-7 cells were also seeded and treated as in MTT assay. The maximum LDH activity was obtained with cells treated with triton 1% for 30 min. The spontaneous control activity was obtained from untreated cells. LDH-released activity in all conditions was assessed in the cell-free supernatants (medium) according to the manufacturer’s instruction (Promega, Madison, WI, USA), spectrophotometrically at 490 nm in a Synergy H1 Hybrid Multi-Mode Microplate Reader (BioTek). The percentage of cytotoxicity was calculated according to the following formula, %Cytotoxicity=Compound-treated LDH activitySpontaneous LDH activity×100Maximum LDH activitySpontaneous LDH activity

Statistical analysis

Data were analyzed by 2-way analysis of variance and post hoc Dunnett’s multiple comparison test (GraphPad Prism, La Jolla, CA, USA), and significant differences were considered at p<0.01.

Results and discussion

Synthesis and characterization of anionic-and cationic-modified CNCs

Amino-functionalized CNCs (CNCs-AMINE) was prepared using simple covalent chemistry via a mild 2-step synthetic approach. The primary alcohol of CNCs was first oxidized via (2,2,6,6-tetramethylpiperidin-1-yl)oxidanyl-mediated oxidation to the corresponding carboxylated CNCs. Subsequently, amidation (1-ethyl-3-(3-dimethylaminopropyl)-carbodiimide/N-hydroxysuccinimide-mediated coupling) with 1,4-diaminobutane afforded the desired CNCs-AMINE (). The chemical and morphological features of CNCs-AMINE were extensively analyzed using a combination of analytical, spectroscopic, and microscopic techniques as previously described.Citation31 The presence of the amino group on the surface of CNCs represents a versatile reactive functional group for a number of bioconjugation strategies as required for bio-applications.

Cyclodextrins (CD), a series of cyclic oligosaccharides, have emerged as attractive building blocks for pharmaceutical and biomedical applications due to their inherent ability to host biologically active molecules and protect them from the external environment.Citation37 As such, CNCs surfaces were covalentlyCitation33 and non-covalentlyCitation38 modified with CD for the design of drug delivery carriers. However, the lack of current cytotoxicity data of CNCs grafted with β-CD further motivated us to synthesize this material following the reported procedure of Lin and Dufresne.Citation33 CNCs-β-CD was obtained by reaction of unmodified CNCs with β-CD in the presence of epichlorohydrin as coupling agent under alkaline condition (). The success of the covalent grafting reaction was confirmed by FT-IR spectroscopy with decrease in peak intensities located at 1163, 1113, and 1059 cm−1 as well as peak broadening at 1031 cm−1 (C-O stretching band) ( and S3 for peak expansion).Citation33 An average grafting efficiency of 15.1 wt% of β-CD covalently grafted on the surface of CNCs was obtained based on the method of weight measurement. Both FT-IR and grafting efficiency results were in good agreement with previously reported values.Citation33 While the above 2 synthetic routes for preparation of anionic-modified CNCs (CNCs-AMINE and CNCs-β-CD) involved simple conjugation chemistries, we further included in our study an anionic and a cationic surface-modified CNCs possessing different polymeric architectures using living radical polymerization technique. CNCs modified with polymeric structures will be useful in further assessing the effect of different surface chemistries on the cytotoxicity of modified CNCs. Polymer grafting on the surface of CNCs can impart its desired properties to CNCs for the development of “smart” materials for biomedical applications. CNCs grafted with poly(N-isopropylacrylamide) (CNCs-poly(NIPAAm)) was prepared and characterized as previously described in our laboratory using the SI-SET-LRP technique ().Citation32 Poly(NIPAAm) is the polymer of choice in this study given its thermoresponsive nature as well as its wide applications in drug delivery and tissue engineering.Citation39 SET-LRP is an emerging robust and versatile polymerization method for designing functional materials with complex molecular architectures in a facile manner.Citation40 Cationic APMA has been previously employed as functional component in the design of drug delivery carriersCitation41,Citation42 and thus, makes it an attractive polymeric material to be coated on the surface of CNCs as well as evaluating its potential cytotoxicity. Using the same SI-SET-LRP approach, the novel CNCs-poly(APMA) was prepared and characterized for its chemical and morphological features using a combination of spectroscopic, microscopic and analytical techniques. When compared with unmodified CNCs (), FT-IR analysis of the purified CNCs-poly(APMA) displayed new FT-IR peaks typical for the amide stretch (1638 cm−1) and amine bend (1538 cm−1) ().Citation36 Upon polymerization, the anionic surface of unmodified CNCs turned cationic as evidenced by zeta potential measurements (). Elemental analysis of CNCs-poly(APMA) indicated an increase in the carbon content and presence of nitrogen that further supported the successful grafting of polymer brushes from the surface of CNCs (Table S1).

Figure 1 FT-IR of (A) unmodified CNCs, (B) CNCs-poly(APMA), (C) CNCs-β-CD.

Abbreviations: CNCs, cellulose nanocrystals; CNCs-β-CD, CNCs grafted with β-cyclodextrin; FT-IR, Fourier transform infrared spectroscopy; poly(APMA), poly(N-3-aminopropyl)methacrylamide; poly(NIPAAm), poly(N-isopropylacrylamide).
Figure 1 FT-IR of (A) unmodified CNCs, (B) CNCs-poly(APMA), (C) CNCs-β-CD.

Table 1 DLS and ζ-potentials for anionic and cationic surface-modified CNCs

STEM was used to visualize the morphologies of the unmodified and modified CNCs (). The STEM images of the unmodified and modified CNCs showed well-dispersed rod-like nanoparticles with size around 100–300 nm in length and 10–20 nm in diameter. In addition to STEM analyses, DLS was used to obtain comparative apparent particle sizes of the modified CNCs as depicted in . However, it is important to note that DLS is routinely used to measure hydrodynamic size of spherical particles and thus, the obtained results do not represent the actual dimensions.

Figure 2 STEM images of unmodified and modified CNCs: (A) unmodified CNCs, (B) CNCs-AMINE, (C) CNCs-poly(NIPAAm), and (D) CNCs-poly(APMA).

Note: Scale bar=100 nm.
Abbreviations: AMINE, amino-functionalized; CNCs, cellulose nanocrystals; CNCs-β-CD, CNCs grafted with β-cyclodextrin; poly(APMA), poly(N-3-aminopropyl)methacrylamide; poly(NIPAAm), poly(N-isopropylacrylamide); STEM, scanning transmission electron microscopy.
Figure 2 STEM images of unmodified and modified CNCs: (A) unmodified CNCs, (B) CNCs-AMINE, (C) CNCs-poly(NIPAAm), and (D) CNCs-poly(APMA).

Given the importance of highly purified materials for the correct interpretation of biological results, all the synthesized modified CNCs were extensively purified by repeated centrifugation and dialysis to ensure efficient removal of unreacted reagents, monomers, and homopolymers prior to all analyses.

Cell viability analysis of surface-modified CNCs

The potential applicability of cellulose-based nanomaterials for biomedical purposes is rapidly emerging, therefore, it is crucial that cytotoxicity studies of modified CNCs are performed in parallel with characterization of these newly synthesized nanomaterials. The cytotoxicity of unmodified and modified CNCs was assessed using both MTT and LDH assays on 2 different cell lines, J774A.1 and MCF-7. The cytotoxicity assay using MTT is based on the conversion of MTT into formazan crystals by living cells, indicating mitochondrial activity that can be associated with percentage of viable cells.Citation43 Results from the MTT assay in J774A.1 cells with 24 h of treatment showed that CNCs-poly(NIPAAm) was the only modified CNCs to significantly decrease cell viability at the intermediate dose (50 µg/mL). At the highest concentration (100 µg/mL), CNCs-AMINE and CNCs-poly(APMA) also had a significantly decreased cell viability similar to previously observed with CNCs-poly(N-[2-aminoethylmethacrylamide]).Citation36 CNCs-β-CD, as well as unmodified CNCs, did not affect cell viability under these tested conditions (). In MCF-7 cells, CNCs-AMINE and CNCs-β-CD did not affect cell viability nor increased the conversion of MTT into formazan with 24 h of treatment. However, CNCs-poly(NIPAAm) increased the conversion of MTT into formazan, even at the lowest concentration (). A similar effect was also observed with CNCs grafted with poly(N-[2-aminoethylmethacryl-amide]).Citation36 Some studies have indicated that the quantity of formazan crystals produced is not solely dependent on cell number.Citation44,Citation45 The MTT assay is based on the conversion of the tetrazolium dye to formazan mainly by mitochondrial succinic dehydrogenases. However, cytosolic enzymes such as nicotinamide adenine dinucleotide (NADH) reductase and flavin oxidase may also play a role in this conversion.Citation46 In addition, the rate of conversion to formazan has been shown to be linked to the cellular metabolic activity as well as the number of mitochondria present in the cell. Therefore, larger cells with more mitochondria have a higher rate of tetrazolium conversion.Citation47 As such, this apparent increase in percentage of viable cells seen in MCF-7 cells might be explained by a potential effect in increases on mitochondrial activity, which is not necessarily associated with increases in cell viability and proliferation.

Figure 3 Cytotoxicity of unmodified and modified CNCs on J774A.1 (A) and MCF-7 (B) cells.

Notes: After 24 h of treatment, cell viability was determined by MTT assay. Data are expressed as percentage of control (non-treated cells, 100% viability) using the mean value and SD from triplicate experiments. *p<0.01 compared to control.
Abbreviations: AMINE, amino-functionalized; CNCs, cellulose nanocrystals; CNCs-β-CD, CNCs grafted with β-cyclodextrin; MTT, 4,5-dimethylthiazol-2-yl-2,5-diphenyltetrazolium bromide; poly(APMA), poly(N-3-aminopropyl)methacrylamide; poly(NIPAAm), poly(N-isopropylacrylamide).
Figure 3 Cytotoxicity of unmodified and modified CNCs on J774A.1 (A) and MCF-7 (B) cells.

We also performed LDH activity assay, which indirectly assessed membrane permeability. LDH is a cytosolic enzyme present in many different types of cells and its release to cell medium can be used as an indication of plasma membrane damage. The released LDH can be quantified in the medium by a coupled enzymatic reaction. Initially, LDH catalyzes the conversion of lactate to pyruvate via reduction of NAD + to NADH. Subsequently, diaphorase uses NADH to reduce a tetrazolium salt (INT) to a red formazan product. Therefore, the level of formazan formation is directly proportional to the amount of released LDH in the medium, which is related to membrane damage.Citation48,Citation49 The 24 h exposure data did not demonstrate any significant differences on the LDH activity between medium from control (untreated cells) and from cells treated with unmodified and modified CNCs, in both cell lines (data not shown). Next, we decided to verify whether these cellulose-based nanomaterials somehow developed cytotoxicity over time, by increasing the incubation time to 48 h, in both cell lines. Again, depending on cell type, the modified CNCs displayed substantial differences on the level of toxicity. Data from MTT assay showed that cell viability of J774A.1 was slightly diminished, but statistically significant in almost all concentrations of CNCs tested, including unmodified CNCs (). Interestingly, in MCF-7 cell line, CNCs-AMINE was the only modified CNCs that showed a significant degree of cytotoxicity at all concentrations, but not in a dose-dependent manner. Since this effect is only observed with MTT assay and not with LDH assay, it implies that it is not related to membrane damage. The effect on increased conversion of MTT into formazan in MCF-7 cells is no longer observed for all the CNCs ().

Figure 4 Cytotoxicity of unmodified and modified CNCs on J774A.1 (A) and MCF-7 (B) cells.

Notes: After 48 h of treatment, cell viability was determined by MTT assay. Data are expressed as percentage of control (non-treated cells, 100% viability) using the mean value and SD from triplicate experiments. *p<0.01 compared to control.
Abbreviations: AMINE, amino-functionalized; CNCs, cellulose nanocrystals; CNCs-β-CD, CNCs grafted with β-cyclodextrin; MTT, 4,5-dimethylthiazol-2-yl-2,5-diphenyltetrazolium bromide; poly-(APMA), poly-(N-3-aminopropyl) methacrylamide; poly-(NIPAAm), poly(N-isopropylacrylamide).
Figure 4 Cytotoxicity of unmodified and modified CNCs on J774A.1 (A) and MCF-7 (B) cells.

Upon 48 h of incubation with unmodified and modified CNCs, the level of LDH activity detected in the medium of MCF-7 cells was no different among groups (data not shown). However, in the medium of J774A.1 cells, we observed significant differences in LDH activity between control (non- treated cells) and the modified CNCs-treated groups. With a longer incubation time, CNCs-poly(NIPAAm) exhibited the least increases in the membrane permeability of the cells, since only at 100 µg/mL LDH activity was significantly detected in the medium. The other modified CNCs, however, started to show effects on membrane permeability with concentration as low as 10 µg/mL. Surprisingly, CNC-β-CD showed the strongest effect on the increases in LDH activity at all concentrations tested ().

Figure 5 Cytotoxicity of unmodified and modified CNCs on J774A.1 cells.

Notes: After 48 h of treatment, cell viability was determined by LDH assay. Data are expressed as percentage of cytotoxicity over the control using the mean value and SD from triplicate experiments. *p<0.01 compared to control.
Abbreviations: CNCs, cellulose nanocrystals; CNCs-β-CD, CNCs grafted with β-cyclodextrin; LDH, lactate dehydrogenase; poly-(APMA), poly-(N-3-aminopropyl) methacrylamide; poly-(NIPAAm), poly(N-isopropylacrylamide).
Figure 5 Cytotoxicity of unmodified and modified CNCs on J774A.1 cells.

CD are complex cyclic oligosaccharides with a hydrophobic cavity. As a consequence, they are widely used by the pharmaceutical industry as drug carriers to increase water solubility of numerous hydrophobic molecules.Citation50 However, the hydrophobicity of CD can also cause this polymer to interact with lipophilic macromolecules, such as cholesterol and fatty acids in the biological milieu. In fact, the majority of research involving CD has focused on their ability to manipulate lipid (phospholipids and cholesterol) composition in different cells because these lipophilic macromolecules can be easily entrapped inside the cavity of CD.Citation51 Thus, a potential explanation for CNCs-β-CD to have the greatest effect on the increase of the LDH activity in the cell culture medium may be due to its ability to interact with lipids in the cell membrane therefore affecting membrane permeability. Although some modified CNCs caused a mild decrease in J774A.1 cell viability at 24 h of treatment, the bright field microscopy images revealed that none of the modified CNCs (50 µg/mL) caused major changes in cell morphology, despite all of them interacting with the cells by mainly forming a “cluster” of cells surrounding the nanomaterial (, first column, white arrows). Interestingly, CNCs-AMINE did not only evoke this “cell cluster” effect, but also showed that the small needle-like particles were spread over the cells (, first column, third panel, black arrows). At 48 h, however, we observed some changes in cell morphology with most of the treatments. At this time point, treatment with CNCs-AMINE caused the cells to be enlarged and the images suggested that the small needle-like particles were interacting with the cell membrane most likely by penetrating into the cells (, second column, third panel, black arrows). Interestingly, this modified CNCs was the only one that did not decrease J774A.1 cell viability at 50 µg/mL dose, as shown with the MTT assay ([], white bars). CNCs-poly(NIPAAm) induced the most prominent change in the morphology of the J774A.1 cells after 48 h of treatment, as observed by enlargement and elongation of the cells (, second column, bottom panel, red arrows).

Figure 6 Microscope images of J774A.1 cells treated with unmodified and modified CNCs (50 μg/mL).

Notes: After indicated times of treatment, images of live cells were taken in bright field with inverted microscope at 400× magnification. White arrows indicate nanomaterial-cell aggregates, black arrows indicate membrane-nanomaterial interactions and red arrows indicate cell enlargement and elongation.
Abbreviations: AMINE, amino-functionalized; CNCs, cellulose nanocrystals; CNCs-β-CD, CNCs grafted with β-cyclodextrin; APMA, (N-3-aminopropyl) methacrylamide; NIPAAm, N-isopropylacrylamide.
Figure 6 Microscope images of J774A.1 cells treated with unmodified and modified CNCs (50 μg/mL).

Overall, our results indicate that “cell clustering” effect and changes in cell morphology are cellular phenomena not necessarily directly related to decreases in cell viability. We do not exclude the possibility that these modifications will not lead to cell toxicity with more prolonged treatment with these nanomaterials. However, an early study with different preparations of carbon nanotubes (CNTs) showed that after long exposure (3 days of treatment), suspended CNT-bundles were less cytotoxic than CNT-agglomerates or asbestos in mesothelial cell morphology (MSTO-211H). The cytotoxicity apparently correlated with changes in cell morphology caused by CNT-agglomerates and asbestos, but not with CNT-bundles. The authors conclude that the CNT-agglomerates are bigger, stiffer and more solid (similar to asbestos) than the CNT-bundles and these structural differences of the CNTs are the reason for cytotoxic response of the cells compared with asbestos.Citation52 Overall, our results indicated that there is no direct correlation with decreases in cell viability and increases in cell permeability with ζ-potential or relative size (sphere-equivalent hydrodynamic diameter) of our surface-modified CNCs. This observation is consistent with the previously published work where neither the size nor the surface charge of the ZnO nanoparticles affected their cytotoxicity against U373MG cells.Citation53 However, we do not exclude the possibility that the short length of CNCs derivative may contribute to less nanomaterial agglomeration or cell clustering formation around the CNCs and therefore better distribution onto the cell surface, resulting in less cytotoxicity.

Conclusion

This study examined the impact of surface organic coatings of CNCs on mammalian cell viability. Four different organic functional moieties ranging from simple organic molecules to complex polymeric structures were covalently conjugated on the surface of CNCs using different synthetic strategies. The in vitro toxicity of the modified CNCs using MTT and LDH assays was assessed on 2 different cell lines, J774A.1 and MCF-7, and unmodified and modified CNCs displayed marginal, but statistically significant decreases in cell viability depending on cell type and the period of incubation. Overall, the results indicated that cells exposed to surface-coated CNCs for 24 h did not show major changes in cell viability, membrane permeability as well as cell morphology. However, at longer exposures, this scenario changed and more in-depth toxicological studies are needed to fully evaluate the biological interactions and safety of these surface-modified CNCs in humans and other mammals, as well as evaluation of immunogenicity, since some of the effects on biological systems are not directly related to cytotoxicity.

Acknowledgments

The authors thank SUNY Plattsburgh for a SUNY Presidential Research Award 2016–2017, the University of Alberta and the National Institute for Nanotechnology and National Research Council of Canada for supporting this project.

Supplementary materials

Fourier transform infrared spectroscopy peak expansion of CNCs-β-CD; 1H NMR and 13C NMR spectra of APMA; elemental analysis of CNCs-poly(APMA).

FT-IR spectroscopy of CNCs-β-CD

Elemental analysis

The percent carbon (C), hydrogen (H), nitrogen (N) and sulphur (S) contents (%) of the unmodified and cationic nanocrystalline cellulose were determined by Carlo Erba CHNS-O EA1108 Elemental Analyzer (Thermo Scientific, Waltham, MA, USA). The remaining sample was assumed to be oxygen (O).

Nuclear magnetic resonance (NMR)

The NMR spectra were recorded on a Bruker 400 MHz spectrometer (Bruker, Billerica, MA, USA). The NMR data is presented as follows: chemical shift δ (ppm), multiplicity, coupling constant and integration. The following abbreviations were used to explain the multiplicities: s=singlet, d=doublet, t=triplet. The 1H NMR and 13C NMR spectra were calibrated using 3-(trimethylsilyl)-1-propanesulfonic acid sodium salt (TMS=0.0) as the internal reference.

Figure S1 1H NMR of cationic monomer APMA.

Abbreviation: APMA, poly(N-3-aminopropyl)methacrylamide; 1H NMR, proton nuclear magnetic resonance.

Figure S1 1H NMR of cationic monomer APMA.Abbreviation: APMA, poly(N-3-aminopropyl)methacrylamide; 1H NMR, proton nuclear magnetic resonance.

Figure S2 13C NMR data of cationic monomer APMA.

Abbreviation: APMA, poly(N-3-aminopropyl)methacrylamide; 13C NMR, carbon nuclear magnetic resonance.

Figure S2 13C NMR data of cationic monomer APMA.Abbreviation: APMA, poly(N-3-aminopropyl)methacrylamide; 13C NMR, carbon nuclear magnetic resonance.

Figure S3 FT-IR of freeze-dried sample of CNCs-β-CD showing peak expansion of key peaks.

Note: Green line: unmodified CNCs, red line: CNCs-poly(APMA), blue line: CNCs-β-CD.

Abbreviations: CNCs, cellulose nanocrystals; CNCs-β-CD, CNCs grafted with β-cyclodextrin; FT-IR, Fourier transform infrared spectroscopy.

Figure S3 FT-IR of freeze-dried sample of CNCs-β-CD showing peak expansion of key peaks.Note: Green line: unmodified CNCs, red line: CNCs-poly(APMA), blue line: CNCs-β-CD.Abbreviations: CNCs, cellulose nanocrystals; CNCs-β-CD, CNCs grafted with β-cyclodextrin; FT-IR, Fourier transform infrared spectroscopy.

Table S1 Elemental analysis of unmodified CNCs and CNCs-poly(APMA)

Disclosure

The authors report no conflicts of interest in this work.

References

  • KlemmDKramerFMoritzSNanocelluloses: a new family of nature-based materialsAngew Chem Int Ed Engl201150245438546621598362
  • MoonRJMartiniANairnJSimonsenJYoungbloodJCellulose nanomaterials review: structure, properties and nanocompositesChem Soc Rev20114073941399421566801
  • HabibiYLuciaLARojasOJCellulose nanocrystals: chemistry, self-assembly, and applicationsChem Rev201011063479350020201500
  • EichhornSJCellulose nanowhiskers: promising materials for advanced applicationsSoft Matter201172303315
  • PengBLDharNLiuHLTamKCChemistry and applications of nanocrystalline cellulose and its derivatives: a nanotechnology perspectiveCan J Chem Eng201189511911206
  • LinNDufresneANanocellulose in biomedicine: current status and future prospectEur Polym J201459302325
  • JorfiMFosterEJRecent advances in nanocellulose for biomedical applicationsJ Appl Polym Sci20151321410974628
  • ShvedovaAAYanamalaNKisinERLong-term effects of carbon containing engineered nanomaterials and asbestos in the lung: One year post-exposure comparisonsAm J Physiol Lung Cell Mol Physiol20143062L170L18224213921
  • SunaseeRHemrazUDCklessKCellulose nanocrystals: a verstatile nanoplatform for emerging biomedical applicationsExpert Opin Drug Deliv20161391243125627110733
  • RomanMToxicity of cellulose nanocrystals: a reviewInd Biotechnol20151112533
  • ShatkinJAKimBCellulose nanomaterials: life cycle risk assessment, and environmental health and safety roadmapEnviron Sci Nano201525477499
  • Camarero-EspinosaSEndesCMuellerSElucidating the potential biological impact of cellulose nanocrystalsFibers20164321
  • RomanMDongSHiraniALeeYWCellulose nanocrystals for drug deliveryEdgarKJHeinzeTBuchananCMPolysaccharide Materials: Performance by DesignWashington, DCAmerican Chemical Society20098191
  • KovacsTNaishVO’ConnorBAn ecotoxicological characterization of nanocrystalline cellulose (NCC)Nanotoxicology20104325527020795908
  • MahmoudKAMenaJAMaleKBHrapovicSKamenALuongJHEffect of surface charge on the cellular uptake and cytotoxicity of fluorescent labeled cellulose nanocrystalsACS Appl Mater Interfaces20102102924293220919683
  • VillanovaJCAyresECarvalhoSMPatricioPSPereiraFVOréficeRLPharmaceutical acrylic beads obtained by suspension polymerization containing cellulose nanowhiskers as excipient for drug deliveryEur J Pharm Sci201142440641521241802
  • JacksonJKLetchfordKWassermanBZYeLHamadWYBurtHMThe use of nanocrystalline cellulose for the binding and controlled release of drugsInt J Nanomedicine2011632133021383857
  • CliftMJFosterEJVanheckeDInvestigating the interaction of cellulose nanofibers derived from cotton with a sophisticated 3D human lung cell cocultureBiomacromolecules201112103666367321846085
  • MaleKBLeungACMontesJKamenALuongJHProbing inhibitory effects of nanocrystalline cellulose: inhibition versus surface chargeNanoscale2012441373137922252333
  • NiHZengSWuJCellulose nanowhiskers: preparation, characterization and cytotoxicity evaluationBiomed Mater Eng20122213121127
  • DongSHiraniAAColacinoKRLeeYWRomanMCytotoxicity and cellular uptake of cellulose nanocrystalsNano Life2012231241006
  • YangXBakaicEHoareTCranstonEDInjectable polysaccharide hydrogels reinforced with cellulose nanocrystals: Morphology, rheology, degradation, and cytotoxicityBiomacromolecules201314124447445524206059
  • PereiraMMRaposoNRBraynerRCytotoxicity and expression of genes involved in the cellular stress response and apoptosis in mammalian fibroblast exposed to cotton cellulose nanofibersNanotechnology201324707510323358497
  • ZoppeJORuottinenVRuotsalainenJSynthesis of cellulose nanocrystals carrying tyrosine sulfate mimetic ligands and inhibition of alphavirus infectionBiomacromolecules20141541534154224628489
  • HanifZAhmedFRShinSWKimYKUmSHSize- and dose-dependent toxicity of cellulose nanocrystals (CNC) on human fibroblasts and colon adenocarcinomaColloids Surf B Biointerfaces201411916216524856254
  • HosseinidoustZAlamMNSimGTufenkjiNvan de VenTGCellulose nanocrystals with tunable surface charge for nanomedicineNanoscale2015740166471665726154822
  • EyleySThielemansWSurface modification of cellulose nanocrystalsNanoscale20146147764777924937092
  • HabibiYKey advances in the chemical modification of nanocellulosesChem Soc Rev20144351519154224316693
  • HemrazUDSunaseeRFunctionalization of Nanocrystalline Cellulose SurfacesDekker Encyclopedia of Nanoscience and Nanotechnology3rd edLyshevskiSEBoca Raton, FLCRC Press2014
  • BolukYLahijiRZhaoLMcDermottMTSuspension viscosities and shape parameter of cellulose nanocrystals (CNC)Colloid Surf A201137713297303
  • HemrazUDBolukYSunaseeRAmine-decorated nanocrystalline cellulose surfaces: synthesis, characterization and surface propertiesCan J Chem20139110974981
  • HemrazUDLuASunaseeRBolukYStructure of poly(N-isopro-pylacrylamide) brushes and steric stability of their grafted cellulose nanocrystal dispersionsJ Colloid Interface Sci201443015716524998068
  • LinNDufresneASupramolecular hydrogels from in situ host-guest inclusion between chemically modified cellulose nanocrystals and cyclodextrinBiomacromolecules201314387188023347071
  • ZhaoQWangSFChengXJYamRCKongDLiRKSurface modification of cellulose fiber via supramolecular assembly of biodegradable polyesters by the aid of host-guest inclusion complexationBiomacro-molecules201011513641369
  • DengZBouchekifHBabooramKHousniAChoytunNNarainRFacile synthesis of controlled-structure primary amine-based methacrylamide polymers via the reversible addition-fragmentation chain transfer processJ Polym Sci Part A Polym Chem2008461549844996
  • HemrazUDCampbellKABurdickJSCklessKBolukYSunaseeRCationic poly(2-aminoethylmethacrylate) and poly(N-(2-aminoeth-ylmethacrylamide) modified cellulose nanocrystals: synthesis, charac-terization, and cytotoxicityBiomacromolecules201516131932525436513
  • Moya-OrtegaMDAlvarez-LorenzoCConcheiroALoftssonTCyclodextrin-based nanogels for pharmaceutical and biomedical applicationsInt J Pharm20124281215216322366058
  • Ndong NtoutoumeGMAGranetRMbakidiJPDevelopment of curcumin-cyclodextrin/cellulose nanocrystals complexes: New anticancer drug delivery systemsBioorg Med Chem Lett201626394194526739777
  • SoodNBhardwajAMehtaSMehtaAStimuli-responsive hydrogels in drug delivery and tissue engineeringDrug Deliv201623375878025045782
  • AnastasakiANikolaouVNurumbetovGCu(0)-mediated living radical polymerization: a versatile tool for materials synthesisChem Rev2016116383587726226544
  • YoonHYKooHChoiKYPhoto-crosslinked hyaluronic acid nanoparticles with improved stability for in vivo tumor-targeted drug deliveryBiomaterials201334215273528023591396
  • YuanJMiaoCPengFSynthesis and characterization of poly(HPMA)-APMA-DTPA-99mTc for imaging-guided drug delivery in hepatocellular carcinomaJ Appl Polym Sci2013127645494556
  • van MeerlooJKaspersGJCloosJCell sensitivity assays: the MTT assayMethods Mol Biol201173123724521516412
  • van TonderAJoubertAMCromartyADLimitations of the 3-(4,5-dimethylthiazol-2-yl)–2,5-diphenyl-2H-tetrazolium bromide (MTT) assay when compared to three commonly used cell enumeration assaysBMC Res Notes201584725884200
  • RissTLMoravecRANilesALBeninkHAWorzellaTJMinorLCell Viability AssaysSittampalamGSAssay Guidance ManualBethesda MDEli Lilly & Company and the National Center for Advancing Translational Sciences2004
  • LuLZhangLWaiMSYewDTXuJExocytosis of MTT formazan could exacerbate cell injuryToxicol In Vitro201226463664422401948
  • JabbarSATwentymanPRWatsonJVThe MTT assay underestimates the growth inhibitory effects of interferonsBr J Cancer19896045235282529890
  • KajaSPayneAJSinghTGhumanJKSieckEGKoulenPAn optimized lactate dehydrogenase release assay for screening of drug candidates in neuroscienceJ Pharmacol Toxicol Methods2015731625681780
  • DeckerTLohmann-MatthesMLA quick and simple method for the quantitation of lactate dehydrogenase release in measurements of cellular cytotoxicity and tumor necrosis factor (TNF) activityJ Immunol Methods1988115161693192948
  • CriniGReview: a history of cyclodextrinsChem Rev201411421109401097525247843
  • LeclercqLInteractions between cyclodextrins and cellular components: towards greener medical applications?Beilstein J Org Chem2016122644266228144335
  • WickPManserPLimbachLKThe degree and kind of agglomeration affect carbon nanotube cytotoxicityToxicol Lett2007168212113117169512
  • KimJEKimHAnSSMaengEHKimMKSongYJIn vitro cytotoxicity of SiO2 or ZnO nanoparticles with different sizes and surface charges on U373MG human glioblastoma cellsInt J Nanomedicine20149Suppl 223524125565841