Influence of prophylaxis paste treatment on the abrasive wear of surface sealants

Abstract

Objective. To investigate the abrasive wear of surface sealants (Seal&Protect and K-0184 (experimental sealant)) and the influence of pre-treatment with mineral deposit forming prophylaxis pastes (NUPRO Sensodyne and NUPRO) on this wear. Methods. One hundred and eight bovine dentine samples were randomly allocated to nine groups (1–9). Pre-treatment (10 s): groups 1–3: untreated, groups 4–6: NUPRO, groups 7–9: NUPRO Sensodyne. Sealing: groups 1, 4 and 7: unsealed, groups 2, 5 and 8: Seal&Protect, groups 3, 6 and 9: K-0184 (experimental sealer). Samples were then brushed with 12 000 brushing strokes (BS) with toothpaste slurry in an automatic brushing machine (120 BS/min; F = 2.5 N). Surface profiles were recorded at baseline, after pre-treatment and sealing and after each 2000 BS. Results. Total profile change (wear or gain due to pre-treatment, treatment and 12 000 BS): groups 1, 4 and 7 (no surface sealant) showed a not significantly different wear of 18.48 ± 2.63 µm, 24.98 ± 3.02 µm and 21.50 ± 5.47 µm, respectively. Remaining groups (sealed) showed a gain in height with no significant difference among each other. Wear in sealed groups (2, 3, 5, 6, 8 and 9) were not significantly different at all numbers of brushing strokes. Starting with 4000 BS, the wear in unsealed groups (1, 4 and 7) was statistically significantly higher compared to all other groups. Conclusion. Stability and wear resistance of surface sealants are not affected by pre-treatment of dentine with NUPRO Sensodyne. The surface sealants tested provide a stable protective surface layer on dentine, which lasts for at least 12 000 brushing strokes.

Key Words::

• abrasion
• dentine
• prophylaxis paste
• surface sealant

Acknowledgement

This study was supported by Dentsply Detrey GmbH, Konstanz, Germany. The funders had no role in study design, data collection and analysis, decision to publish, or preparation of the manuscript.

Declaration of interest: The authors report no conflicts of interest. The authors alone are responsible for the content and writing of the paper.