Effects of ceramic shade and thickness on the micro-mechanical properties of a light-cured resin cement in different shades

Abstract

Objective. The aim of this study was to evaluate the micro-mechanical properties of a light-cured resin cement in four different shades when polymerized through a leucite-reinforced glass-ceramic in different shades and thicknesses. Materials and methods. A light-cured resin cement in four different shades (HV+1, HV+3, LV-1 and LV-3) was selected for this study. The specimens were cured by using a LED-unit (Bluephase®, IvoclarVivadent) for 20 s under a leucite-reinforced glass-ceramic (IPS Empress® CAD, IvoclarVivadent) in two different shades (A1 and A3) of different thicknesses (1 and 2 mm). Specimens cured directly, without an intermediate ceramic, served as control. The specimens were stored after curing for 24 h at 37°C by maintaining moisture conditions with distilled water. Micro-mechanical properties (indentation modulus, E; Hardness, HV; creep, Cr) of the resin cements were measured with an automatic microhardness indenter (Fisherscope H100C, Germany). Twenty groups were included (n = 3), while 10 measurements were performed on each specimen. Data were statistically analyzed by using one-way ANOVA and Tukey’s post-hoc test, as well as a multivariate analysis to test the influence of the study parameters. Results. Significant differences were observed between the micromechanical properties of the tested resin cements (p < 0.05). The resin cement shade showed the highest effect on the micromechanical properties (Partial-eta squared (η_P²)-E = 0.45, η_P²-HV = 0.59, η_P²-Cr = 0.29) of the resin cement, followed by ceramic thickness (η_P²-E = 0.38, η_P²-HV = 0.3, η_P²-Cr = 0.04) and ceramic shade (η_P²-E = 0.2, η_P²-HV = 0.26). Conclusions. Resin cement shade is an important factor influencing the mechanical properties of the material. Light shades of a resin cement express higher E and HV as well as lower Cr values compared with the darker ones.

Key Words:

• Light-cured resin cement
• hardness
• ceramic thickness
• indentation modulus
• micromechanical properties

Declaration of interest: The authors report no conflicts of interest. The authors alone are responsible for the content and writing of the paper.