Scale formation mechanisms of martensitic steels in high CO₂/H₂O-containing gases simulating oxyfuel environments

Abstract

In oxyfuel power plants, metallic components will be exposed to service environments containing high amounts of CO₂ and water vapour. Therefore, the oxidation behaviour of a number of martensitic 9–12%Cr steels in a model gas mixture containing 70% CO₂–30% H₂O was studied in the temperature range 550–700°C. The results were compared with the behaviour in air, Ar–CO₂ and Ar–H₂O. It was found that in the CO₂- and/or H₂O-rich gases, the mentioned steels tended to form iron-rich oxide scales with significantly higher growth rates than the Cr-rich surface scales formed during air exposure. The iron-rich scales were formed as a result of a decreased flux of chromium in the bulk alloy toward the surface because of enhanced internal oxidation of chromium in the H₂O-containing gases and carbide formation in the CO₂-rich gases. Additionally, the presence of water vapour in the exposure atmosphere led to buckling of the outer haematite layer, apparently as a result of compressive oxide growth stresses. The Fe-base oxide scales formed in CO₂(–H₂O)-rich gases appeared to be permeable to CO₂ molecules resulting in substantial carburization of the steel.

Keywords:

• oxyfuel power plants
• scale formation mechanisms
• martensitic steels