A detailed experimental study of the effects of pre-bond contamination with a hydraulic fluid, thermal degradation, and poor curing on fracture toughness of composite-bonded joints

References

• Banea MD, Da Silva LFM. Adhesively bonded joints in composite materials: an overview. Proc. Inst. Mech. Eng. Part L: J. Mater. Des. Appl. 2009;223:1–18.
   PubMed Web of Science ®Google Scholar
• Adams RD. Adhesive bonding: science, technology and applications. Abington Cambridge: Woodhead Publishing; 2005.
   Google Scholar
• Da Silva LFM, Öchsner A. Modeling of adhesively bonded joints. Berlin: Springer; 2008.
   Google Scholar
• Caminero MA, Pavlopoulou S, Lopez-Pedrosa M, Nicolaisson BG, Pinna C, Soutis C. Analysis of adhesively bonded repairs in composites: damage detection and prognosis. Compos. Struct. 2013;95:500–517.
   Web of Science ®Google Scholar
• Hu FZ, Soutis C. Strength prediction of patch-repaired CFRP laminates loaded in compression. Compos. Sci. Technol. 2000;60:1103–1114.
   Web of Science ®Google Scholar
• Cheng P, Gong XJ, Hearn D, Aivazzadeh S. Tensile behaviour of patch-repaired CFRP laminates. Compos. Struct. 2011;93:582–589.
   Web of Science ®Google Scholar
• Ecault R, Boustie M, Berthe L, Touchard F, Voillaume H, Campagne B, Loison D. Development of a laser shock wave adhesion test for the detection of weak composite bonds. 5th International Symposium on NDT in Aerospace; 2013 November 13–15; Singapore.
   Google Scholar
• Opoka S, Malinowski P, Wandowski T, Skarbek L, Ostachowicz W. Damage detection using electromechanical impedance technique combined with scanning laser vibrometry. Key Eng. Mater. 2013;569–570:687–694.
   Google Scholar
• Markatos DN, Tserpes KI, Rau E, Markus S, Ehrhart B, Pantelakis Sp. The effects of manufacturing-induced and in-service related bonding quality reduction on the mode-I fracture toughness of composite bonded joints for aeronautical use. Composites Part B. 2013;45:556–564.
   Web of Science ®Google Scholar
• Markatos DN, Tserpes KI, Rau E, Brune K, Pantelakis Sp. Degradation of mode-I fracture toughness of CFRP bonded joints due to release agent and moisture pre-bond contamination. J. Adhes. 2013;90:156–173.
   Google Scholar
• Skydrol 500 hydraulic fluid resistance of EC 1290 Scotchweld prime and AF 10 adhesive bonded joints. Convair Report. 1958. (no. 58-371).
   Google Scholar
• Tomblin J, Salah L. Effects of repair procedures on bonded repairs of composite structures. JAMS Technical Review; 2011.
   Google Scholar
• Choi DM, Park CK, Cho K, Park CE. Adhesion improvement of epoxy resin/polyethylene joints by plasma treatment of polyethylene. Polymer. 1997;38:6243–6249.
   Web of Science ®Google Scholar
• Ochoa-Putman C, Vaidya UK. Mechanisms of interfacial adhesion in metal–polymer composites – effect of chemical treatment. Composites Part A: Appl. Sci. Manuf. 2011;42:906–915.
   Web of Science ®Google Scholar
• Aydın MD, Temiz Ş, Özel A. Effect of curing pressure on the strength of adhesively bonded joints. J. Adhes. 2007;83:553–571.
   Web of Science ®Google Scholar
• Rider AN, Chalklev PD. The effect of FM-73 cure temperature on the durability of bonded joints employing BR127 primer. Defence Science and Technology Organisation (Australia), Melbourne: Aeronautical and Maritime Research Laboratory; 2000.
   Google Scholar
• ISO 15024. Fibre-reinforced plastic composites – determination of mode I interlaminar fracture toughness, GIC, for unidirectionally reinforced materials; 2001.
   Google Scholar
• Airbus. IPS-01-006-02 curing cycle for release test specimens, issue 4; June 2008.
   Google Scholar
• O'brien RG. A general ANOVA method for robust tests of additive models for variances. J. Am. Stat. Assoc. 1979;74:877–880.
   Web of Science ®Google Scholar
• One-way ANOVA followed by Tukey’s multiple comparisons test was performed using GraphPad Prism version 6.00 for Windows, GraphPad Software, La Jolla, CA, www.graphpad.com.
   Google Scholar
• Jaccard J, Becker MA, Wood G. Pairwise multiple comparison procedures: a review. Psychol. Bull. 1984;96:589–596.
   Web of Science ®Google Scholar
• Wu L, Hoa SV, Ton-That M-T. Effects of water on the curing and properties of epoxy adhesive used for bonding FRP composite sheet to concrete. J. Appl. Polym. Sci. 2004;92:2261–2268.
   Web of Science ®Google Scholar
• Humfeld GR, Dillard DA. Residual stress development in adhesive joints subjected to thermal cycling. J. Adhes. 1998;65:277–306.
   Web of Science ®Google Scholar
• Djokic D, Johnston A, Rogers A, Lee-Sullivan P, Mrad N. Residual stress development during the composite patch bonding process: measurement and modeling. Composites Part A: Appl. Sci. Manuf. 2002;33:277–288.
   Web of Science ®Google Scholar
• ASTM D5573. Standard practice for classifying failure modes in fiber-reinforced-plastic (FRP) joints; 2012.
   Google Scholar