Metallurgical reasons for hot cracking in repair of the corrosion‐resisting lining of a pressure vessel

References

• Sinai , J . 1986 . ‘Optimisation of the two‐layer buttering procedure of repair welding underbead cracks without preheating and heat treatment’ , Progress report Bratislava : Publ Welding Research Institute .
   Google Scholar
• Folkhard , E . 1988 . ‘Welding metallurgy of stainless steels’ , Vienna : Publ Springer‐Verlag .
   Google Scholar
• Kujanpaa , V . 1979 . Weld Res Int , : 55
   Google Scholar
• Cemy , V . ‘Reasons for the formation of cracks in 25Cr10NiNb deposits’ , Report of MV Plzen : Publ ZES .
   Google Scholar
• Ellinger , J and Kricka , P . 1991 . Zvaranie , 40 (1) : 1
   Google Scholar
• Hrivnak , I . 1986 . ‘Examination of the nature of defects in multilayer deposits produced with a wide strip under a flux’ , Technical report Bratislava : Publ Welding Research Institute .
   Google Scholar
• Sefcik , D . 1982 . ‘Verification of the properties of the developmental strip electrode Sv04Kh20N10G2B’ , Bratislava : Publ Welding Research Institute .
   Google Scholar
• Barborka , J . 1992 . ‘Possibilities of automaticgas shielded arc welding in repairing WER 440 reactors’ . Zvaranie , 41 (9) : 199
   Google Scholar