A comparison between the levels of preheat temperature necessary to prevent cold cracking during welding of low-alloy high- and higher-strength steels

References

• ‘Recommendations for arc welding of ferrite steels’ Proposal for prEN 1011: 1993 standard
   Google Scholar
• Oct 1993 . ‘Correct welding of fine constructional steels. Guidelines for the manufacture – especially for fusion welding. Prevention of cold cracking in welding; ensuring correct preheat temperature’ Oct , SEW 088 guidelines, Beiblatt, 4th issue
   Google Scholar
• Ito , Y and Bessyo , K . ‘A prediction of welding procedure to avoid heat affected zone cracking’ IIW Doc IX–631–69
   Google Scholar
• Suzuki , H . ‘Cold cracking and its prevention in steel welding’ IIW Doc IX–1074–78
   Google Scholar
• Suzuki , H . ‘Cold cracking and its prevention in steel welding. Report 2 – root cracking’ IIW Doc IX–1110–79
   Google Scholar
• Suzuki , H . ‘Cold cracking and its prevention in steel welding. Report 3 – effects of heat input and restraint’ IIW Doc IX–1157–80
   Google Scholar
• Brozda , J . 1983 . ‘Factors influencing cold cracking in butt-welded joints’ . Prace Insytutu Spawalnictwa , (4)
   Google Scholar
• 1974 . ‘Specification for metal-arc welding of carbon and carbon manganese steels’ BS 5135
   Google Scholar
• Seminar . March 1994 . ‘Recommendation of European standard for the welding of construction steels’ , March , Publ Instytut Spawalnictwa .
   Google Scholar
• Uwer , D and Hohne , H . 1991 . ‘Characteristics of cold cracking in welded steels’ . Schweissen und Schneiden , (43) (IIW Doc IX–1631–91)
   Google Scholar
• ‘Studies on structural restraint severity relating to weld cracking in Japan’ IIW Doc IX–986–76
   Google Scholar
• Szczecinski , Z . 1971 . “ ‘Calculation of preheat temperatures in steel welding’ ” . In Biuletyn Instytutu Spawalnictwa (47a)
   Google Scholar
• Brozda , J . 1974 . “ ‘Development of a programme for the provision of information for the welding material chart’ ” . In Instytut Spawalnictwa Research Report (Gg-28/III)
   Google Scholar
• Brozda , J . 1977 . “ ‘Description of characteristic features of weldability of steels at temperatures up to −60°C’ ” . In Instytut Spawalnictwa Research Report (Id–69)
   Google Scholar
• Zeman , N . “ ‘Characteristic features of the weldability of 10G2AV and 10G2A VNb steels’ ” . In Instytut Spawalnictwa Research Report 1077 (Id–67)
   Google Scholar
• Debski , E . 1977 . “ ‘Characteristic features of the weldability of semi-killed C-Mn steel with micro-alloys’ ” . In Instytut Spawalnictwa Research Report (Id–70)
   Google Scholar
• Brozda , J . 1990 . “ ‘Weldability of the toughened Polish steels’ ” . In Prace Instytutu Spawalnictwa (1)
   Google Scholar
• Ochodek , V . ‘Comments on the optimisation of preheat temperatures’ . Proc 19th int ‘Welding’ congress . Bratislava .
   Google Scholar
• ‘Investigations into the tendency to cold cracking in arc-welded joints’ Polish Standard PN-90/M-69760
   Google Scholar
• Kubica , M . 1992 . “ ‘Investigation into the weldability of low-alloy steels with yield stresses exceeding 800 MPa’ ” . In Instytut Spawalnictwa Research Report (Ac-68)
   Google Scholar
• Brozda , J . 1995 . “ ‘A review of the preheat temperatures preventing cold cracking during the welding of high- and higher- strength steels’ ” . In Instytut Spawalnictwa Research Report (Da–79) (Problem No 1)
   Google Scholar