Fabrication of coloured zirconia ceramics by infiltrating water debound injection moulded green body

, , , &
Pages 58-62 | Received 22 Apr 2009, Accepted 27 Jun 2009, Published online: 22 Nov 2013

References

  • German RM: ‘Powder injection molding’; 1990, Princeton, NJ, MPIF.
  • Song JH, Evans JRG: ‘The injection‐molding of fine and ultra‐fine zirconia powders’, Ceram. Int., 1995, 21, (5), 325–333.
  • Song JH, Edirisinghe MJ, Evans JRG, Twizell EH: ‘Modeling the effect of gas transport on the formation of defects during thermolysis of powder moldings’, J. Mater. Res., 1996, 11, (4), 830–840.
  • Huzzard RJ, Blackburn S: ‘Influence of solids loading on aqueous injection moulding paste’, Br. Ceram. Trans., 1999, 98, (2), 49–56.
  • Soykan HS, Karakas Y: ‘Injection moulding of thin walled zirconia tubes for oxygen sensors’, Adv. Appl. Ceram., 2005, 104, (6), 285–290.
  • Shaw HM, Edirisinghe MJ: ‘Porosity development during removal of organic vehicle from ceramic injection moldings’, J. Eur. Ceram. Soc., 1994, 13, (2), 135–142.
  • Shaw HM, Edirisinghe MJ: ‘Shrinkage and particle packing during removal of organic vehicle from ceramic injection moldings’, J. Eur. Ceram. Soc., 1995, 15, (2), 109–116.
  • Bakan HI: ‘Injection moulding of alumina with partially water soluble binder system and solvent debinding kinetics’, Mater. Sci. Technol., 2007, 23, (7), 787–791.
  • Yang WW, Yang KY, Wang MC, Hon MH: ‘Solvent debinding mechanism for alumina injection molded compacts with water‐soluble binders’, Ceram. Int., 2003, 29, (7), 745–756.
  • Krauss VA, Oliveira AAM, Klein AN, Al‐Qureshi HA, Fredel MC: ‘A model for PEG removal from alumina injection moulded parts by solvent debinding’, J. Mater. Process. Technol., 2007, 182, (1–3), 268–273.
  • Hu SC, Hwang KS: ‘Length change and deformation of powder injection‐molded compacts during solvent debinding’, Metall. Mater. Trans. A, 2000, 31A, (5), 1473–1478
  • Liu DM, Tseng WJ: ‘Influence of debinding rate, solid loading and binder formulation on the green microstructure and sintering behaviour of ceramic injection mouldings’, Ceram. Int., 1998, 24, (6), 471–481
  • Shivashankar TS, German RM: ‘Effective length scale for predicting solvent‐debinding times of components produced by powder injection molding’, J. Am. Ceram. Soc., 1999, 82, (5), 1146–1152
  • Song JH, Evans JRG, Edirisinghe MJ, Twizell EH: ‘Effect of powder bed on critical heating rates for thermolysis of ceramic injection moldings’, AIChE J., 1996, 42, (6), 1715–1722
  • Aboushelib MN, Kleverlaan CJ, Feilzer AJ: ‘Effect of zirconia type on its bond strength with different veneer ceramics’, J. Prosthodont., 2008, 17, (5), 401–408
  • Pittayachawan P, McDonald A, Petrie A, Knowles JC: ‘The biaxial flexural strength and fatigue property of Lava (TM) Y‐TZP dental ceramic’, Dent. Mater., 2007, 23, (8), 1018–1029
  • Schabbach LM, Bondioli F, Ferrari AM, Manfredini T, Petter CO, Fredel MC: ‘Color in ceramic glazes: analysis of pigment and opacifier grain size distribution effect by spectrophotometer’, J. Eur. Ceram. Soc., 2008, 28, (9), 1777–1781
  • Chiou YH, Lin ST: ‘Influence of CoO and Al2O3 on the phase partitioning of ZrO2‐3 mol% Y2O3’, Ceram. Int., 1996, 22, (3), 249–256.
  • Fujisaki H: ‘Zirconia‐containing powder for black zirconia sintered body, e.g. for ornamental articles such as watch bands, contains specified amount of cobalt–zinc–iron–aluminum or aluminum oxide containing pigment, aluminum oxide, and yttrium oxide’, European patent no. EP1857428A1, 21 November 2007.
  • Marple BR, Green DJ: ‘Mullite alumina particulate composites by infiltration processing’, J. Am. Ceram. Soc., 1989, 72, (11), 2043–2048
  • Albano MP, Scian AN: ‘Mullite/SiAlON/alumina composites by infiltration processing’, J. Am. Ceram. Soc., 1997, 80, (1), 117–124.
  • Glass SJ, Green DJ: ‘Permeability and infiltration of partially sintered ceramics’, J. Am. Ceram. Soc., 1999, 82, (10), 2745–2752.
  • Marple BR, Green DJ: ‘Graded compositions and microstructures by infiltration processing’, J. Mater. Sci., 1993, 28, (17), 4637–4643.
  • Washburn EW: ‘The dynamics of capillary flow’, 1921, , 374–375 College Park, MD, American Physical Society.
  • Einset EO: ‘Capillary infiltration rates into porous media with applications to Silcomp processing’, J. Am. Ceram. Soc., 1996, 79, (2), 333–338
  • ‘Colorimetry’; 1986, Vienna, Central Bureau of the Commission Internationale de l'Eclairage.

Reprints and Corporate Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

To request a reprint or corporate permissions for this article, please click on the relevant link below:

Academic Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

Obtain permissions instantly via Rightslink by clicking on the button below:

If you are unable to obtain permissions via Rightslink, please complete and submit this Permissions form. For more information, please visit our Permissions help page.