Glass Transition Behavior of Spray Dried Orange Juice Powder Measured by Differential Scanning Calorimetry (DSC) and Thermal Mechanical Compression Test (TMCT)

, , , &
Pages 661-673 | Received 18 Mar 2006, Accepted 09 Nov 2006, Published online: 10 Aug 2007
 

Abstract

Spray drying behavior of orange juice concentrate with various levels of maltodextrin (DE 6) was studied. Five combinations of orange juice concentrate and maltodextrin (25:75, 30:70, 35:65, 40:60, and 50:50) were spray dried at 160 and 65°C inlet and outlet temperatures, respectively. The product recovered with 50% maltodextrin concentration was sticky and only 20% powder was recovered. The recovery of orange juice powder increased as the amount of maltodextrin in powders increased. The particle size and bulk density remained almost the same in all except in 50% maltodextrin powder which was slightly larger and more dense. The moisture content of spray dried powders was high and desiccated before measuring glass transition temperature. The anhydrous spray dried powders showed increased Tg values with increasing maltodextrin concentration, from 66°C in 50% maltodextrin to 97°C in 75% maltodextrin containing powders. The glass rubber transition (Tg-r) values of all the products measured using novel Thermal Mechanical Compression Test (TMCT) were higher than Tg values measured by DSC; the difference in values increased with increase in maltodextrin concentration.

Reprints and Corporate Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

To request a reprint or corporate permissions for this article, please click on the relevant link below:

Academic Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

Obtain permissions instantly via Rightslink by clicking on the button below:

If you are unable to obtain permissions via Rightslink, please complete and submit this Permissions form. For more information, please visit our Permissions help page.