Effect of amine structure on CO₂ capture by polymeric membranes

Abstract

Poly(amidoamine)s (PAMAMs) incorporated into a cross-linked poly(ethylene glycol) exhibited excellent CO₂ separation properties over H₂. However, the CO₂ permeability should be increased for practical applications. Monoethanolamine (MEA) used as a CO₂ determining agent in the current CO₂ capture technology at demonstration scale was readily immobilized in poly(vinyl alcohol) (PVA) matrix by solvent casting of aqueous mixture of PVA and the amine. The resulting polymeric membranes can be self-standing with the thickness above 3 μm and the amine fraction less than 80 wt%. The gas permeation properties were examined at 40 °C and under 80% relative humidity. The CO₂ separation performance increased with increase of the amine content in the polymeric membranes. When the amine fraction was 80 wt%, the CO₂ permeability coefficient of MEA containing membrane was 604 barrer with CO₂ selectivity of 58.5 over H₂, which was much higher than the PAMAM membrane (83.7 barrer and 51.8, respectively) under the same operation conditions. On the other hand, ethylamine (EA) was also incorporated into PVA matrix to form a thin membrane. However, the resulting polymeric membranes exhibited slight CO₂-selective gas permeation properties. The hydroxyl group of MEA was crucial for high CO₂ separation performance.

Keywords:

• Amine structure
• CO₂
• gas permeation
• membrane
• separation

Classification:

• 50 Energy Materials
• 105 Low-Dimension (1D/2D) materials
• 206 Energy conversion / transport / storage / recovery

Acknowledgements

The authors thank Shigenori Fujikawa for use of the SEM apparatus.