ABSTRACT
The isothermal bainite transformation in low-carbon low-alloy steel under direct and step-quenching conditions have been investigated in the present work. Varying quantities of prior bainite and prior martensite were formed separately by quenching above and below temperature to understand their effects on the extent and kinetics of subsequent bainite transformation in
regime. Formation of prior bainite at higher temperature has been found to stabilise part of remaining austenite against subsequent bainite transformation at lower temperature showing thermal stabilisation of austenite. Hence, the total amount of bainite in two-step treatment is less than that obtained in single-step isothermal bainite transformation at the latter temperature, indicating the inapplicability of ‘additivity rule’ for continuously cooled bainite. A decrease in the bainitic ferrite plate volume due to higher strength of parent austenite and higher nucleation rate, together with limited number of bainite nucleation sites at the latter temperature are believed to be responsible for the thermal stabilisation of austenite. Prior martensite also stabilises part of remaining austenite against further bainite transformation through fragmentation of austenite grains and increased defect density in austenite. The kinetics of bainite transformation in each of the above-mentioned conditions have been analysed quantitatively using an established model and the results are correlated with the microstructures.
Acknowledgements
The authors gratefully acknowledge the financial support from Indian Institute of Technology. Authors are thankful to all the staff members of Steel Technology Centre and Central Research Facility for providing various research facilities and assistance.
Disclosure statement
No potential conflict of interest was reported by the authors.
Correction Statement
This article has been republished with minor changes. These changes do not impact the academic content of the article.