Migration of melamine from can coatings cross-linked with melamine-based resins, into food simulants and foods

, , &
Pages 243-250 | Received 26 Jul 2010, Accepted 25 Oct 2010, Published online: 21 Dec 2010
 

Abstract

Resins based on melamine-formaldehyde and related analogues such as methylolated melamine are used to cross-link coatings used inside food cans and on the metal closures of glass jars. Thirteen commercially coated cans and closures representing 80% of the European market were tested using simulants under realistic industrial heat-processing conditions for canned and jarred foods. The food simulants and the retort conditions used were 3% acetic acid for 1 h at 100°C and 10% ethanol for 1 h at 130°C. The highest migration level seen for melamine into simulant was 332 µg kg−1. There was no detectable migration of the melamine analogues cyanuric acid (<1 µg kg−1) or ammelide (<5 µg kg−1) from any sample. Twelve of the thirteen samples released no detectable ammeline (<5 µg kg−1) but the coating giving the highest release of melamine did also release ammeline at 8 µg kg−1 with the higher of the two process temperatures used. Migration experiments into food simulant and foods themselves were then conducted using two experimental coatings made using amino-based cross-linking resins. Coated metal panels were exposed to the food simulant 10% (v/v) aqueous ethanol and to three foodstuffs under a range of time and temperature conditions both in the laboratory and in a commercial food canning facility using proprietary time and temperature conditions. The highest migration into a food was 152 µg kg−1 from the first coating processed for a long time at a moderate sterilisation temperature. The highest migration into simulant was also from this coating at 220 µg kg−1 when processed at 134°C for 60 min, dropping to 190 µg kg−1 when processed at 123°C for 70 min. Migration from the second coating was quite uniformly two to three times lower under all tests. These migration results were significantly higher than the levels of melamine extractable using 95% ethanol at room temperature. The experiments show that commercial canning and retorting can be mimicked in an acceptable way using laboratory tests with an autoclave or a simple pressure cooker. The results overall show there is hydrolytic degradation of the melamine cross-linked resins to release additional melamine. There is a strong influence of the temperature of heat treatment applied with foods or simulants but only a minor influence of time of heating and only a minor influence, if any, of food/simulant acidity.

Acknowledgements

Mike Reid (PPG Packaging Coatings, London) and David Smith (Metal Packaging Manufacturers Association, UK) kindly organised the preparation and provision of the simulant samples for the ring trial of the 13 commercial coatings. The Valspar Corporation provided the two experimental coatings for the second set of food and simulant tests, the H. J. Heinz Company heat-processed those samples, and the two companies co-funded that phase of the work.

Reprints and Corporate Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

To request a reprint or corporate permissions for this article, please click on the relevant link below:

Academic Permissions

Please note: Selecting permissions does not provide access to the full text of the article, please see our help page How do I view content?

Obtain permissions instantly via Rightslink by clicking on the button below:

If you are unable to obtain permissions via Rightslink, please complete and submit this Permissions form. For more information, please visit our Permissions help page.