Effect of ceramic material type on the fracture load of inlay-retained and full-coverage fixed dental prostheses

, , &
Pages 62-70 | Received 05 Jun 2019, Accepted 03 Mar 2020, Published online: 30 Mar 2020
 

Abstract

Objective

Ceramic inlay-retained fixed partial denture (IRFPD) is a conservative prosthetic option but the mechanical durability of new high strength zirconia reinforced glass ceramic FPDs is not investigated. The purpose of this study was to compare fracture load of 3-unit ceramic FPDs.

Materials and methods

Extracted premolars and molars (N = 64) were used to create three test groups (IRFPDs) and one control group (full coverage FPD) (n = 8). The teeth were embedded in PMMA resin with a mesiodistal distance of 6 mm. Premolars had a distal and molars had a mesial inlay preparation (width: 3 mm; height: 4 mm) in the test groups. IRFPDs were made from a zirconia reinforced lithium silicate (VS) or a monolithic zirconia. Zirconia IRFPDs received 2 types of surface treatments: sandblasting (Zr-IRFPD) or internal coating with feldspathic porcelain (ZrC-IRFPD). Control group was made from monolithic zirconia with the same connector size and zirconia surfaces were sandblasted (Zr-FPD). All restorations were cemented using a resin luting cement. After 5000 thermo-cycles, fracture load values (N) were determined with a universal testing machine at a crosshead speed of 0.75 mm/min. Data were analyzed using 1-way ANOVA and Tukey`s post hoc test (p ˂ .05).

Result

Fracture load (mean ± SD) of Zr-FPDs, Zr-IRFPDs and ZrC-IRFPDs were 672 ± 183, 672 ± 123 and 638 ± 59, respectively, being not statistically different (p > .05). VS-IRFPD exhibited statically lower values (391 ± 136). The predominant mode of failure was fracture at the connector area in all groups.

Conclusion

The fracture load of 3-unit IRFPD was significantly affected by types of ceramics but the retainer design and surface treatment in Zr groups did not show a significant effect.

Disclosure statement

No potential conflict of interest was reported by the author(s).

Additional information

Funding

This research did not receive any specific grant from funding agencies in the public, commercial, or not-for-profit sectors.