Microstructure and tensile properties of Al_0.5CoCrCuFeNi alloys produced by simple rolling and annealing

Abstract

This study demonstrates that simply by rolling at ambient temperature, FCC type high entropy alloy Al_0.5CoCrCuFeNi can be refined to have nanocrystalline structure and exhibits outstanding combination of strength and ductility. The yield strength and ultimate tensile strength are 1284 and 1344 MPa, respectively, in combination with an elongation of 7.6%. After a short annealing at 900°C for 10 min, the elongation is doubled to 15.3% with a trade-off around 20% in strength. This excellent combination of strength and ductility is attributable to the activation of quasi-dynamic recrystallisation during cold work and the limited grain growth during 900°C annealing.

Keywords:

• High entropy alloys
• Nanostructured metals
• Rolling and annealing
• Mechanical properties