Effects of different surface treatments of zirconia on the bond strength of self-adhesive resinous cement

Abstract

Purpose: The aim of this study was to evaluate the effects of different zirconia surface treatments on the bond strength of two self-adhesive resinous cements (SARC).

Methods: Two hundred and eight cylindrical specimens were obtained from Y-TZP zirconia (half with diameter 3.2 mm and half with 4.8 mm). After sintering and polishing, specimens were divided into four groups (n = 26), according to surface treatment: Control (no treatment); Sandblasting (Al₂O₃ particles); Rocatec (Al₂O₃ particles, tribochemical silica coating and silane application); Laser (Nd: YAG laser: 20 Hz, 100 mJ, 0.2 J/cm²). The surface roughness (Ra) was evaluated after the surface treatments, and the groups were divided into two subgroups (n = 13), according to the SARC tested: RelyX U200 and Bifix SE. The 2.2-mm cylinders were bonded to 4.8-mm cylinders and stressed until failure under shear using a universal testing machine. Bond strength and Ra were analyzed using ANOVA, and Tukey’s test (α = 0.05).

Results: Surface treatment was significant (p < 0.0001), but cement type (p = 0.73) was not. Related to roughness, significant differences were found for the treatment type (p < 0.0001), with laser being the treatment with higher Ra values.

Conclusions: Nd:YAG laser produced a rougher surface and a higher bond strength compared with sandblasting, silicatization, and control groups.

Keywords:

• Zirconia
• Nd:YAG Laser
• surface treatments
• bond strength
• self-adhesive cement