Complex reaction behaviour of ceramic mould with the molten AZ91 alloy during investment casting

Abstract

The effects of different pouring temperatures on the reaction behaviour of the ceramic shell with the molten Mg-9%Al-1%Zn-0.4%Mn (all are in wt-%) (AZ91) alloy during investment casting were studied. The scanning electron microscopy (SEM) micrographs with energy dispersive spectroscopy (EDS) analysis illustrated a complex interaction behaviour of the alloy with the mould components at various pouring temperatures. The MgO + MgAl₂O₄ compounds were formed on the surface of investment cast alloy at the pouring temperature of 600°C. With increasing the temperature to 650°C, the MgO compounds with the Al₂O₃ particles were observed at the interface of metal/mould. The Al₂O₃ particles were the main compound on the surface of alloy at the pouring temperature of 700°C. The formation of Al₂O₃ particles instead of the MgO compounds on the surface was related to the increase of magnesium evaporation by enhancement of the pouring temperature and also diffusion of Al₂O₃ particles from the ceramic shell to the surface of the alloy.

KEYWORDS:

• AZ91 alloy
• investment casting
• pouring temperature
• interaction layer
• ceramic mould

Disclosure statement

No potential conflict of interest was reported by the author(s).