ABSTRACT
In this paper, the hydrophilic UiO-66-NH2 nanomaterial was synthesized by the solvent-thermal method and characterized. Then, UiO-66-NH2 was introduced into the casting membrane solution of cellulose acetate (CA) forward osmosis (FO) membrane, and CA/UiO-66-NH2 forward osmosis membrane was prepared by the phase inversion method. The optimum preparation conditions of CA/UiO-66-NH2 mixed matrix membranes were determined as follows: the content of UiO-66-NH2 was 0.4 wt%, the coagulation bath temperature was 35°C, the mixing temperature was 50°C and the heat treatment temperature was 50°C. FTIR, SEM, water contact angle and AFM were carried out on CA/UiO-66-NH2 forward osmosis membrane prepared under the best preparation conditions. Compared to the CA forward osmosis membrane, the permeability and selectivity of the CA/UiO-66-NH2 membrane were improved. The water flux and reverse salt flux of the CA/UiO-66-NH2 forward osmosis membrane reached 52.32 L/(m2·h) and 2.43 g/(m2·h), respectively. The permeability selectivity of CA membranes and CA/UiO-66-NH2 membranes did not change much during 180 min, indicating that the two membranes had good long-term stability. This study shows a potential advantage of UiO-66-NH2 as additives for improvement in the desalination performance of forward osmosis membranes.
Disclosure statement
No potential conflict of interest was reported by the author(s).
Data availability statement
The authors confirm that the data supporting the findings of this study are available within the article.