ABSTRACT

In the present study, laser surface melting (LSM) of 304L stainless steel (SS) was performed using 250 W pulse Nd: YAG laser which resulted in a 250 µm thick melted layer with refined microstructure on the surface. Potentiostatic polarisations at various potentials in the transpassive regime in 6 M HNO₃ solution at 95°C were used to quantify the IGC rate. The transpassive dissolution rate was significantly reduced after LSM. The pitting corrosion susceptibility was assessed by potentiodynamic polarisation in 3.5 wt-% NaCl solution. LSM resulted in an increase in pitting potential. Following electrochemical tests, sample surfaces were examined using optical and scanning electron microscopes besides a 3-D optical profilometer. The depths of IGC attack and pit were significantly reduced after LSM. The improvement in resistance to pitting corrosion and transpassive dissolution was attributed to the elimination of inclusions and impurity segregation at the grain boundaries brought about by LSM.

KEYWORDS:

• Laser surface melting
• stainless steel
• transpassive dissolution
• intergranular corrosion
• pitting corrosion
• polarisation

Acknowledgement

Technical assistance of Mr. Pawan Kumar during laser surface melting experiments is thankfully acknowledged.

Disclosure statement

No potential conflict of interest was reported by the author(s).