Effect of Al₂O₃ nanoparticles on the steel-glass/epoxy composite joint bonded by a two-component structural acrylic adhesive

Abstract

This paper reports a study on the effect of Al₂O₃ nanoparticles on the adhesion strength of steel-glass/epoxy composite joints bonded by a two-component structural acrylic adhesive. The addition of Al₂O₃ nanoparticles to the two-component acrylic adhesive led to a remarkable enhancement in the shear and tensile strength of the composite joints. The shear and tensile strength of the adhesive joints increased by addition of Al₂O₃ up to 1.5 wt%, which decreased by further addition of the nanofiller. Introduction of the nanoparticles caused a reduction in the peel strength of the joints. DSC analysis revealed that the glass transition temperature (Tg) of the adhesives rose by increasing the nanofiller content. The advancing water contact angle was decreased for adhesives containing nanoparticles. SEM micrographs indicated good dispersions of the Al₂O₃ nanoparticles within the acrylic matrix in the specimens with up to 1.5 wt% Al₂O₃ and revealed that addition of nanoparticles altered the fracture morphology from smooth to rough fracture surfaces.

Keywords:

• Acrylic adhesive
• adhesion properties
• adhesive bonded joint Al₂O₃ nanoparticle
• nanoadhesive