Developing a steady state wear equation for AA7050 hybrid composites/steel interface at elevated temperature

ABSTRACT

In this research work, an attempt was made to reinforce AA7050/5Gr composites with multi-walled carbon nanotube (MWCNT) of varying weight percentages processed through stir casting route. SEM with EDS mapping revealed that the particles were uniformly distributed over the composites. Hardness reduces with increasing MWCNT weight percentage owing to the inverse hall petch effect and increment in void content. A third-body abrasion, which happens when the CNT in the aluminium matrix material detaches from the surface and erodes material from the composites pin as well as the counter face, causes the wear resistance to rise with the addition of CNT particles. A mechanically mixed layer, which avoids direct metal-to-metal contact and thus increases wear resistance, was created at the abraded surface and at high temperature, where the reduction of wear rate was due to the development of oxide protective layer. A steady-state wear equation for the contacting surface at high temperature (R = 1/Y √(ln W/2X)) for AA7050 hybrid composites–steel interface was developed. The enhancement in wear resistance was directly proportional to the proportion of ferrous content present on the surface, which was confirmed on the elemental analysis. Pock marks, micropits, craters and cracks were the features observed on the worn surface morphology, whereas delamination and plasticisation were the observed modes of wear mechanism.

KEYWORDS:

• High-temperature tribology
• hardness
• wear equation
• worn surface morphology
• carbon nanotubes

Disclosure statement

No potential conflict of interest was reported by the author(s).