Capsule-free hot isostatic pressing of sintered steel to full density using water atomised iron and Cr-alloyed powder consolidated by cold isostatic pressing

References

• German RM. Powder metallurgy of iron and steel. New York, NY: John Wiley & Sons; 1998.
   Google Scholar
• Dale JR. Powder metallurgy -Intrinsically Sustainable. Int J Powder Metall. 2011;47:27–31.
   Web of Science ®Google Scholar
• German RM, Myers N, Mueller T, et al. An analysis of approaches to high-performance powder metallurgy. Powder Met. 2004;2004:76–88.
   Google Scholar
• Hryha E, Vattur Sundaram M, Weddeling A, et al. Hot Isostatic Pressing of the Water Atomised Steel Powder: Possibilities and Challenges. World PM 2018. 2018.
   Google Scholar
• Åslund C, Eklund A. Preform CIP for fully dense PM parts. Powder Met. 2012;2012:3126–3132.
   Google Scholar
• Vattur Sundaram M. Novel approaches for acheiving full density powder metallurgy steels. Gothenburg: Chalmers University of Technology; 2019.
   Google Scholar
• Abkowitz S, Abkowitz S, Fisher H. Breakthrough claimed for titanium PM. Met Powder Rep. 2011;66(6):16–21.
   Google Scholar
• Price PE. Cold isostatic pressing. Powder Metall, ASM handbook. Powder Met Technol Appl ASM International. 2015;7:255–259.
   Google Scholar
• James PJ. Particle deformation during cold isostatic pressing of Metal powders. Powder Metall. 1977;20:199–204.
   Web of Science ®Google Scholar
• German RM. Particle packing characteristics. Princeton, NJ: Metal Powder Industries Federation; 1989.
   Google Scholar
• Schatt W, Wieters KP. Powder metallurgy - processing and materials. Shrewsbury: EPMA; 1997.
   Google Scholar
• Eisen WB, Ferguson BL, German RM, et al. Powder Metal Technologies and Applications. New York, NY: ASM International; 1998.
   Google Scholar
• Vattur Sundaram M, Khodaee A, Andersson M, et al. Experimental and finite element simulation study of capsule-free hot isostatic pressing of sintered gears. Int J Adv Manuf Technol. 2018;99:1725–1733.
   Web of Science ®Google Scholar
• German RM. Green body homogeneity effects on sintered tolerances. Powder Metall. 2004;47:157–160.
   Web of Science ®Google Scholar
• Oikonomou C, Hryha E, Ahlin Å, et al. Effect of powder properties on the compressibility of water-atomized iron and Low-alloyed steel grades. Euro PM2013. 2013;2:205–212.
   Google Scholar
• German RM. Powder metallurgy science. 2nd ed. Princeton, NJ: Metal Powder Industries Federation; 1984.
   Google Scholar
• Hryha E, Nyborg L. Oxide transformation in Cr-Mn-prealloyed sintered steels: thermodynamic and kinetic aspects. Metall Mater Trans A. 2014;45:1736–1747.
   Google Scholar
• Chasoglou D, Hryha E, Nyborg L. Effect of process parameters on surface oxides on chromium-alloyed steel powder during sintering. Mater Chem Phys. 2013;138:405–415.
   Web of Science ®Google Scholar
• Campos M, Sanchez D, Torralba JM. Sintering behaviour improvement of a low Cr-Mo prealloyed powder steel through Mn additions and others liquid phase promoters. J Mater Process Technol. 2003;143–144:464–469.
   Web of Science ®Google Scholar
• Gierl C, Danninger H. Chemical reactions during sintering of Cr-Mo prealloyed powder compacts in inert and reducing atmospheres. Adv Powder Metall Part Mater - 2009, Proc 2009 Int Conf Powder Metall Part Mater PowderMet. 2009;2009:511–522.
   Google Scholar
• Thümmler F, Oberacker R. An Introduction to powder metallurgy. London: The Institute of Materials; 1993.
   Google Scholar
• Dlapka M, Danninger H, Gierl C, et al. Defining the pores in PM components. Met Powder Rep. 2010;65:30–33.
   Google Scholar
• Flodin A, Andersson M, Miedzinski A. Full density powder metal components through Hot isostatic pressing. Met Powder Rep. 2017;72:107–110.
   Google Scholar
• Hassanin H, Al-Kinani AA, ElShaer A, et al. Stainless steel with tailored porosity using canister-free hot isostatic pressing for improved osseointegration implants. J Mater Chem B. 2017;5:9384–9394.
   PubMed Web of Science ®Google Scholar
• Essa K, Jamshidi P, Zou J, et al. Porosity control in 316L stainless steel using cold and hot isostatic pressing. Mater Des. 2018;138:21–29.
   Web of Science ®Google Scholar
• Hatami S, Malakizadi A, Nyborg L, et al. Critical aspects of sinter-hardening of prealloyed Cr-Mo steel. J Mater Process Technol. 2010;210:1180–1189.
   Web of Science ®Google Scholar
• Magnusson H, Gårdstam J, Kaplan B, et al. Atmosphere control during hot isostatic pressing of capsule-free materials. Virtual Congress Euro PM2020; 2020.
   Google Scholar
• Andersson M, Bergendahl M, Bjarre U, et al. Manufacturing full density powder metallurgy gears through HIP:ing. Met Powder Rep. 2019;74:199–203.
   Google Scholar
• Ahlfors M. The possibilities and advantages with Heat treatments in HIP. HIP'14, 11th Int Conf Hot Isostatic Press, Stockholm, Sweden; 2014.
   Google Scholar
• Weddeling A, Theisen W. Energy and time saving processing: A combination of hot isostatic pressing and heat treatment. Met Powder Rep. 2017;72:345–348.
   Google Scholar