Evaluation of susceptibility of hydrogen-induced cracking in micro-alloyed armour steel welds using a geometry-modified implant test

References

• Espejo , E , Castro , A and Martinez , L . 2001 . Deformation and fracturing mechanisms present in the formation of craters resulting from the impact of projectiles on steel plates . Eng Investig , 48 : 12 – 19 . ISSN 0120-5609, Columbia
   Google Scholar
• Ade , F . 1991 . Ballistic qualification of armour steel weldments . Weld J. USA , 70 : 53 – 58 .
   Google Scholar
• Madhusudhan Reddy , G and Mohandas , T . 1996 . Ballistics performance of high strength low alloy steel weldments . J Mater Process Tech. Holland , 57 ( 12 ) : 23 – 30 .
   Google Scholar
• Giraldo J, Unfried J. Characterisation of welds in MIL A46100 steels with stainless electrodes. XIX Congress on Naval Engineering, COPINAVAL. Guayaquil (Ecuador) 2005. [cited 2009 May 10]. Available from: www.ipen.org.br/articulos2.html
   Google Scholar
• Mohandas , T , Madhusudhan Reddy , G and Satish Kumar , B . 1999 . Heat affected zone softening in high strength low alloy steels . Mater Proc Tech. Holland , 88 ( 1–3 ) : 284 – 294 .
   Google Scholar
• Giraldo JE, Chaves CA. Hydrogen induced cracking in steel welds. Revista Dyna. Columbia, Vol. 132, 2001. p. 59–64. [cited 2009 June 4]. Available from: www2.unalmed.edu.co/dyna2005/132/agrietamietno.html
   Google Scholar
• Magudeeswaran , G and Balasubramanian , VG . 2008 . Effect of welding process and consumables on tensile and impact properties of high strength quenched and tempered steel joints . J Iron Steel Res Int. Holland , 15 ( 6 ) : 87 – 94 .
   Web of Science ®Google Scholar
• Madhusudhan Reddy , G , Mohandas , T and Papukutty , KK . 1998 . Effect of welding process on the ballistic performance of high strength low alloy steel weldments . J Mater Proc Tech. Holland , 74 ( 1–3 ) : 27 – 35 .
   Google Scholar
• American Welding Society . 1998 . Standard methods for mechanical testing of welds , B4.0-98 USA : American Welding Society .
   Google Scholar
• Military Standard 1941. QX117.3 Weld procedure. Standard code indents. SD-X12140D. USA; 1987
   Google Scholar
• Chapeau W, Baus R. Application of welding to construction, No.3: Mechanical Tests related to welded assemblies. France; 1978. 300 p
   Google Scholar
• Dadian , M . 1985 . Cold cracking test methods using implants . Weld World. France , 23 ( 1 ) : 12 – 21 .
   Google Scholar
• Hart , P and Watkinson , F . 1972 . Development and use of the implant cracking test . Weld J. USA , : 349 – 357 .
   Google Scholar
• Unfried Silgado J. Welding features of an armouring steel using high resistance ferritic support material. [Dissertation (Masters)] Faculty of Mining [Medellin]: National University of Columbia; 2005. 185 p
   Google Scholar
• Unfried Silgado , J , Torres Lopez , E , Giraldo , J and Bastidas , U . 2007 . Influence of the state of consumables and pre-heating on susceptibility to hydrogen induced cracking in welding armouring steel . Latin Am Met Mater Mag. Venezuela , 27 ( 2 ) : 114 – 123 . [cited 2009 June 4]. Available from: www.scielo.org/pdf/rlmm/v27n/art06.pdf
   Google Scholar
• American Welding Society. Structural welding code AWS D1.1. USA; 1998
   Google Scholar
• Magudeeswaran , G , Balasubramanian , V and Madhusudhan Reddy , G . 2008 . Hydrogen induced cold cracking studies on armour grade high strength, quenched and tempered steel weldments . Inter J Hydr Energy. Germany , 33 : 1897 – 1908 .
   Google Scholar
• Unfried Silgado , J , Garzón , CM and Giraldo , JE . 2009 . Numerical and experimental analysis of microstructure evolution during arc welding in armour plate steels . J Mater proc Tech. Holland , 209 ( 4 ) : 1688 – 1700 .
   Google Scholar