Evaluation of creep rupture behaviour for weld joint and base metal of the Cr35Ni45Nb alloy

References

• Shinozaki K, Kuroki H, Nakao Y, et al. Deterioration of weldability of long-term aged HP heat-resistant cast steel containing Nb, Mo, and W. Weld Int. 1999;13(1):39–48. doi: 10.1080/09507119909452053
   Google Scholar
• Ul-Hamid A, Tawancy HM, Mohammed A-RI, et al. Failure analysis of furnace radiant tubes exposed to excessive temperature. Eng Fail Anal. 2006;13(6):1005–1021. doi: 10.1016/j.engfailanal.2005.04.003
   Web of Science ®Google Scholar
• Chun CM, Desai S, Hershkowitz F, et al. Materials challenges in cyclic carburizing and oxidizing environments for petrochemical applications. Mater Corros. 2014;65(3):282–295. doi: 10.1002/maco.201307059
   Web of Science ®Google Scholar
• Kaya AA. Microstructure of HK40 Alloy after high-temperature service in oxidizing/carburizing environment – II. Carburization and Carbide Transformations. Mater Charact. 2002;49(1):23–34. doi: 10.1016/S1044-5803(02)00284-X
   Web of Science ®Google Scholar
• Kaya AA, Krauklis P, Young DJ. Microstructure of HK40 alloy after high temperature service in oxidizing/carburizing environment – I. Oxidation phenomena and propagation of a crack. Mater Charact. 2002;49(1):11–21. doi: 10.1016/S1044-5803(02)00249-8
   Web of Science ®Google Scholar
• Petkovicluton R, Ramanarayanan TA. Mixed-oxidant attack of high-temperature alloys in carbon- and oxygen-containing environments. Oxid Met. 1990;34(5–6):381–400. doi: 10.1007/BF00664423
   Web of Science ®Google Scholar
• Gong JM, Tu ST, Yoon KB. Damage assessment and maintenance strategy of hydrogen reformer furnace tubes. Eng Fail Anal. 1999;6(3):143–153. doi: 10.1016/S1350-6307(98)00042-9
   Web of Science ®Google Scholar
• Konosu S, Koshimizu T, Iijima T, et al. Evaluation of creep-fatigue damage interaction in HK40 alloy. J Mech Des. 1993;115(1):41–46. doi: 10.1115/1.2919322
   Web of Science ®Google Scholar
• Branza T, Deschaux-Beaume F, Sierra G, et al. Study and prevention of cracking during weld-repair of heat-resistant cast steels. J Mater Process Technol. 2009;209(1):536–547. doi: 10.1016/j.jmatprotec.2008.02.033
   Web of Science ®Google Scholar
• Allahkaram SR, Borjali S, Khosravi H. Investigation of weldability and property changes of high pressure heat-resistant cast stainless steel tubes used in pyrolysis furnaces after a five-year service. Mater Des. 2012;33:476–484. doi: 10.1016/j.matdes.2011.04.052
   Web of Science ®Google Scholar
• Shen LM, Gong JM, Jiang Y, et al. Effects of aging treatment on microstructure and mechanical properties of Cr25Ni35Nb and Cr35Ni45Nb furnace tube steel. Acta Metall Sinica-English Lett. 2011;24(3):235–242.
   Web of Science ®Google Scholar
• Sustaita-Torres IA, Haro-Rodríguez S, Guerrero-Mata MP, et al. Aging of a cast 35Cr–45Ni heat resistant alloy. Mater Chem Phys. 2012;133(2–3):1018–1023. doi: 10.1016/j.matchemphys.2012.02.010
   Web of Science ®Google Scholar
• Srisuwan N, Eidhed K, Kreatsereekul N, et al. The study of heat treatment effects on chromium carbide precipitation of 35Cr–45Ni–Nb alloy for repairing furnace tubes. Metals (Basel). 2016;6(1): 1–14.
   Web of Science ®Google Scholar
• Mostafaei M, Shamanian M, Purmohamad H, et al. Microstructural degradation of Two cast heat resistant reformer tubes after long term service exposure. Eng Fail Anal. 2011;18(1):164–171. doi: 10.1016/j.engfailanal.2010.08.017
   Web of Science ®Google Scholar
• Babakr A, Habiby F. Lengthening, cracking and weldability problems of Fe–Ni–Cr alloy tube. J Minerals Mater Charact Eng. 2009;8(02):133–148.
   Google Scholar
• Haro S, Mendoza E, Rodríguez J, Colás R. Microstructural analysis of heat-resistant welded pipes. Mater Charact. 2003;51:21–27. doi: 10.1016/j.matchar.2003.09.005
   Web of Science ®Google Scholar
• Attarian M, Taheri AK, Jalilvand S, et al. Microstructural and failure analysis of welded primary reformer furnace tube made of HP-Nb micro alloyed heat resistant steel. Eng Fail Anal. 2016;68:32–51. doi: 10.1016/j.engfailanal.2016.05.023
   Web of Science ®Google Scholar
• Mostafaei M, Shamanian M, Purmohamad H, et al. Increasing weldability of service-aged reformer tubes by partial solution annealing. J Mater Eng Perform. 2016;25(4):1291–1303. doi: 10.1007/s11665-016-1973-z
   Web of Science ®Google Scholar
• A.A.R. Dehmolaei, M. Shamanian. The effect of aging treatment of HP steel on the microstructure, mechanical properties and its weldability to Incoloy 800. International Conference on Materials Heat Treatment (ICMH 2010); 2010.
   Google Scholar
• Singhatham C, Eidhed K. Effect of carburizing on microstructure and weldability of 35Cr–45Ni–Nb alloys in the ethylene heating furnace. Appl Mech Mater. 2016;848:39–42. doi: 10.4028/www.scientific.net/AMM.848.39
   Google Scholar
• Singhatham C, Eidhed K. The study of welding repair parameters of tube 35Cr–45Ni–Nb alloy of the ethylene heating furnace. Appl Mech Mater. 2016;848:35–38. doi: 10.4028/www.scientific.net/AMM.848.35
   Google Scholar
• Shiga K, Hara Y, Yamamoto E. Repair welding of long-term used ethylene pyrolysis radiant tubes. New York: Amer Soc Mech Eng; 2008. p. 433–438.
   Google Scholar
• Dehmolaei R, Shamanian M, Kermanpur A. Effect of solution annealing on weldability of aged alloy 800/25cr-35ni steel dissimilar welds. Sci Technol Weld Joining. 2008;13(6):515–523. doi: 10.1179/174329308X345074
   Web of Science ®Google Scholar
• Laigo J, Christien F, Le Gall R, et al. SEM, EDS, EPMA-WDS and EBSD characterization of carbides in HP type heat resistant alloys. Mater Charact. 2008;59(11):1580–1586. doi: 10.1016/j.matchar.2008.02.001
   Web of Science ®Google Scholar
• Rodriguez J, Haro S, Velasco A, et al. A metallographic study of aging in a cast heat-resisting alloy. Mater Charact. 2000;45(1):25–32. doi: 10.1016/S1044-5803(00)00047-4
   Web of Science ®Google Scholar